		J·K^-1 mol^-1						kJ·mol^-1
Aluminum (Al)								Al₁(l)

Enthalpy Reference Temperature = T_r = 298.15 K								Standard State Pressure = p° = 0.1 MPa
T/K		C_p^°		S^°		-[G^°-H^°(T_r)]/T		H-H^°(T_r)		_fH^°		_fG^°		log K_f
0
100
200
250

298.15		24.209		39.549		39.549		0.		10.562		7.201		-1.262

300		24.247		39.699		39.550		0.045		10.562		7.180		-1.250
350		25.113		43.505		39.848		1.280		10.562		6.617		-0.987
400		25.784		46.904		40.522		2.553		10.562		6.053		-0.790
450		26.335		49.973		41.404		3.856		10.562		5.489		-0.637
500		26.842		52.774		42.403		5.186		10.562		4.926		-0.515

600		27.886		57.759		44.557		7.921		10.562		3.798		-0.331
700		29.100		62.146		46.762		10.769		10.562		2.671		-0.199

720.000		29.371		62.969		47.201		11.353		GLASS <--> LIQUID
720.000		31.751		62.969		47.201		11.353		TRANSITION

800		31.751		66.315		48.948		13.893		10.706		1.535		-0.100
900		31.751		70.054		51.089		17.068		10.740		0.384		-0.022

933.450		31.751		71.213		51.790		18.131		CRYSTAL <--> LIQUID

1000		31.751		73.400		53.156		20.244		0. 0. 0.

1100		31.751		76.426		55.136		23.419		0.		0.		0.
1200		31.751		79.189		57.027		26.594		0.		0.		0.
1300		31.751		81.730		58.831		29.769		0.		0.		0.
1400		31.751		84.083		60.552		32.944		0.		0.		0.
1500		31.751		86.273		62.194		36.119		0.		0.		0.

1600		31.751		88.323		63.764		39.294		0.		0.		0.
1700		31.751		90.247		65.266		42.469		0.		0.		0.
1800		31.751		92.062		66.704		45.644		0.		0.		0.
1900		31.751		93.779		68.085		48.819		0.		0.		0.
2000		31.751		95.408		69.410		51.994		0.		0.		0.

2100		31.751		96.957		70.686		55.169		0.		0.		0.
2200		31.751		98.434		71.914		58.344		0.		0.		0.
2300		31.751		99.845		73.098		61.519		0.		0.		0.
2400		31.751		101.196		74.240		64.694		0.		0.		0.
2500		31.751		102.493		75.345		67.870		0.		0.		0.

2600		31.751		103.738		76.413		71.045		0.		0.		0.
2700		31.751		104.936		77.447		74.220		0.		0.		0.

2790.812		31.751		105.986		78.359		77.103		FUGACITY = 1 bar

2800		31.751		106.091		78.450		77.395		293.901 0.968 0.018
2900		31.751		107.205		79.422		80.570		-292.806		11.479		-0.207
3000		31.751		108.281		80.366		83.745		-291.710		21.953		-0.382

PREVIOUS: June 1979								CURRENT: June 1983

Aluminum (Al)								Al₁(l)

Download table in tab-delimited text format.