		J·K^-1 mol^-1						kJ·mol^-1
Aluminum (Al)								Al₁(cr,l)

Enthalpy Reference Temperature = T_r = 298.15 K								Standard State Pressure = p° = 0.1 MPa
T/K		C_p^°		S^°		-[G^°-H^°(T_r)]/T		H-H^°(T_r)		_fH^°		_fG^°		log K_f
0		0.		0.		INFINITE		-4.539		0.		0.		0.
100		12.997		6.987		47.543		-4.056		0.		0.		0.
200		21.338		19.144		30.413		-2.254		0.		0.		0.
250		23.084		24.108		28.668		-1.140		0.		0.		0.

298.15		24.209		28.275		28.275		0.		0.		0.		0.

300		24.247		28.425		28.276		0.045		0.		0.		0.
350		25.113		32.231		28.574		1.280		0.		0.		0.
400		25.784		35.630		29.248		2.553		0.		0.		0.
450		26.335		38.699		30.130		3.856		0.		0.		0.
500		26.842		41.501		31.129		5.186		0.		0.		0.

600		27.886		46.485		33.283		7.921		0.		0.		0.
700		29.100		50.872		35.488		10.769		0.		0.		0.
800		30.562		54.850		37.663		13.749		0.		0.		0.
900		32.308		58.548		39.780		16.890		0.		0.		0.

933.450		32.959		59.738		40.474		17.982		CRYSTAL <--> LIQUID
933.450		31.751		71.213		40.474		28.693		TRANSITION

1000		31.751		73.400		42.594		30.806		0.		0.		0.

1100		31.751		76.426		45.534		33.981		0.		0.		0.
1200		31.751		79.189		48.225		37.156		0.		0.		0.
1300		31.751		81.730		50.706		40.331		0.		0.		0.
1400		31.751		84.083		53.007		43.506		0.		0.		0.
1500		31.751		86.273		55.153		46.681		0.		0.		0.

1600		31.751		88.323		57.162		49.856		0.		0.		0.
1700		31.751		90.247		59.052		53.031		0.		0.		0.
1800		31.751		92.062		60.836		56.207		0.		0.		0.
1900		31.751		93.779		62.525		59.382		0.		0.		0.
2000		31.751		95.408		64.129		62.557		0.		0.		0.

2100		31.751		96.957		65.656		65.732		0.		0.		0.
2200		31.751		98.434		67.112		68.907		0.		0.		0.
2300		31.751		99.845		68.505		72.082		0.		0.		0.
2400		31.751		101.196		69.839		75.257		0.		0.		0.
2500		31.751		102.493		71.120		78.432		0.		0.		0.

2600		31.751		103.738		72.350		81.607		0.		0.		0.
2700		31.751		104.936		73.535		84.782		0.		0.		0.

2790.812		31.751		105.986		74.574		87.665		FUGACITY = 1 bar

2800		31.751		106.091		74.677		87.957		293.901 0.968 0.018
2900		31.751		107.205		75.780		91.132		-292.805		11.479		-0.207
3000		31.751		108.281		76.846		94.307		-291.710		21.953		-0.382

PREVIOUS:								CURRENT: June 1983

Aluminum (Al)								Al₁(cr,l)

Download table in tab-delimited text format.