fH°fG°| Lithium Aluminum Oxide (LiAlO2) | Al1Li1O2(cr) | |||||||||||||
| Enthalpy Reference Temperature = Tr = 298.15 K | Standard State Pressure = p° = 0.1 MPa | |||||||||||||
| J·K-1 mol-1 | kJ·mol-1 | |||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| T/K | Cp° | S° | -[G°-H°(Tr)]/T | H-H°(Tr) | fH° |
fG° |
log Kf | |||||||
| 0 | 0. | 0. | INFINITE | -9.693 | -1180.523 | -1180.523 | INFINITE | |||||||
| 100 | 17.966 | 8.046 | 99.257 | -9.121 | -1183.834 | -1165.875 | 608.991 | |||||||
| 200 | 47.999 | 30.154 | 58.942 | -5.758 | -1187.025 | -1146.565 | 299.452 | |||||||
| 298.15 | 67.777 | 53.313 | 53.313 | 0. | -1188.674 | -1126.303 | 197.324 | |||||||
| 300 | 68.128 | 53.733 | 53.314 | 0.126 | -1188.693 | -1125.916 | 196.039 | |||||||
| 400 | 81.546 | 75.421 | 56.180 | 7.697 | -1189.202 | -1104.891 | 144.284 | |||||||
| 500 | 88.408 | 94.425 | 61.974 | 16.226 | -1192.298 | -1083.492 | 113.192 | |||||||
| 600 | 92.688 | 110.947 | 68.790 | 25.294 | -1192.108 | -1061.744 | 92.433 | |||||||
| 700 | 95.751 | 125.475 | 75.871 | 34.723 | -1191.706 | -1040.047 | 77.609 | |||||||
| 800 | 98.165 | 138.424 | 82.896 | 44.423 | -1191.220 | -1018.414 | 66.496 | |||||||
| 900 | 100.203 | 150.107 | 89.725 | 54.343 | -1190.737 | -996.843 | 57.855 | |||||||
| 1000 | 102.006 | 160.759 | 96.303 | 64.455 | -1200.889 | -974.563 | 50.906 | |||||||
| 1100 | 103.654 | 170.559 | 102.614 | 74.740 | -1200.170 | -951.964 | 45.205 | |||||||
| 1200 | 105.198 | 179.645 | 108.660 | 85.183 | -1199.326 | -929.436 | 40.457 | |||||||
| 1300 | 106.671 | 188.124 | 114.450 | 95.777 | -1198.363 | -906.983 | 36.443 | |||||||
| 1400 | 108.089 | 196.082 | 119.999 | 106.515 | -1197.279 | -884.609 | 33.005 | |||||||
| 1500 | 109.466 | 203.586 | 125.324 | 117.393 | -1196.075 | -862.317 | 30.029 | |||||||
| 1600 | 110.813 | 210.694 | 130.439 | 128.408 | -1194.752 | -840.109 | 27.427 | |||||||
| 1700 | 112.140 | 217.452 | 135.361 | 139.556 | -1338.549 | -810.812 | 24.913 | |||||||
| 1800 | 113.449 | 223.899 | 140.102 | 150.835 | -1336.240 | -779.835 | 22.630 | |||||||
| 1900 | 114.746 | 230.068 | 144.676 | 162.245 | -1333.827 | -748.988 | 20.591 | |||||||
| 1973.000 | 115.679 | 234.411 | 147.916 | 170.656 | CRYSTAL <--> LIQUID | |||||||||
| 2000 | 116.022 | 235.986 | 149.094 | 173.784 | 1331.309 718.272 18.759 | |||||||||
| 2100 | 117.294 | 241.678 | 153.368 | 185.449 | -1328.691 | -687.684 | 17.105 | |||||||
| 2200 | 118.558 | 247.163 | 157.508 | 197.242 | -1325.971 | -657.223 | 15.604 | |||||||
| PREVIOUS: June 1972 | CURRENT: December 1979 | |||||||||||||
| Lithium Aluminum Oxide (LiAlO2) | Al1Li1O2(cr) | |||||||||||||
Download table in tab-delimited text format.