		J·K^-1 mol^-1						kJ·mol^-1
Lithium Aluminum Oxide (LiAlO₂)								Al₁Li₁O₂(l)

Enthalpy Reference Temperature = T_r = 298.15 K								Standard State Pressure = p° = 0.1 MPa
T/K		C_p^°		S^°		-[G^°-H^°(T_r)]/T		H-H^°(T_r)		_fH^°		_fG^°		log K_f
0
100
200

298.15		67.777		93.711		93.711		0.		-1107.739		-1057.412		185.254

300		68.128		94.131		93.712		0.126		-1107.758		-1057.100		184.057
400		81.546		115.820		96.578		7.697		-1108.267		-1040.115		135.825
500		88.408		134.823		102.372		16.226		-1111.362		-1022.756		106.847

600		92.688		151.345		109.189		25.294		-1111.172		-1005.048		87.497
700		95.751		165.874		116.270		34.723		-1110.771		-987.390		73.680
800		98.165		178.822		123.294		44.423		-1110.285		-969.797		63.321
900		100.203		190.505		130.124		54.343		-1109.801		-952.266		55.268
1000		102.006		201.158		136.702		64.455		-1119.953		-934.026		48.789

1100		103.654		210.958		143.013		74.740		-1119.234		-915.467		43.472
1200		105.198		220.044		149.058		85.183		-1118.391		-896.979		39.044
1300		106.671		228.523		154.848		95.777		-1117.427		-878.566		35.301
1400		108.089		236.480		160.398		106.515		-1116.343		-860.232		32.096

1450.000		108.784		240.285		163.087		111.937		GLASS <--> LIQUID
1450.000		125.520		240.285		163.087		111.937		TRANSITION

1500		125.520		244.541		165.732		118.213		-1114.319		-841.994		29.321

1600		125.520		252.642		170.913		130.765		-1111.459		-823.932		26.899
1700		125.520		260.251		175.947		143.317		-1253.851		-798.873		24.546
1800		125.520		267.426		180.832		155.869		-1250.271		-772.213		22.409
1900		125.520		274.212		185.570		168.421		-1246.715		-745.751		20.502

1973.000		125.520		278.945		188.937		177.584		CRYSTAL <--> LIQUID

2000		125.520		280.651		190.164		180.973		1243.184 719.476 18.791

2100		125.520		286.775		194.620		193.525		-1239.679		-693.377		17.247
2200		125.520		292.614		198.943		206.077		-1236.201		-667.443		15.847
2300		125.520		298.194		203.137		218.629		-1232.750		-641.669		14.573
2400		125.520		303.536		207.210		231.181		-1229.327		-616.043		13.408
2500		125.520		308.660		211.166		243.733		-1225.934		-590.560		12.339

2600		125.520		313.583		215.011		256.285		-1222.571		-565.211		11.355
2700		125.520		318.320		218.750		268.837		-1219.240		-539.991		10.447
2800		125.520		322.885		222.388		281.389		-1509.843		-513.926		9.587
2900		125.520		327.289		225.930		293.941		-1505.483		-478.435		8.618
3000		125.520		331.545		229.380		306.493		-1501.159		-443.093		7.715

3100		125.520		335.660		232.743		319.045		-1496.871		-407.895		6.873
3200		125.520		339.645		236.021		331.597		-1492.620		-372.835		6.086
3300		125.520		343.508		239.220		344.149		-1488.408		-337.907		5.349
3400		125.520		347.255		242.343		356.701		-1484.235		-303.106		4.657
3500		125.520		350.894		245.393		369.253		-1480.103		-268.428		4.006

3600		125.520		354.430		248.373		381.805		-1476.013		-233.866		3.393
3700		125.520		357.869		251.286		394.357		-1471.966		-199.418		2.815
3800		125.520		361.216		254.135		406.909		-1467.963		-165.078		2.269
3900		125.520		364.477		256.922		419.461		-1464.005		-130.843		1.752
4000		125.520		367.654		259.651		432.013		-1460.094		-96.710		1.263

PREVIOUS: June 1972								CURRENT: December 1979

Lithium Aluminum Oxide (LiAlO₂)								Al₁Li₁O₂(l)

Download table in tab-delimited text format.