		J·K^-1 mol^-1						kJ·mol^-1
Lithium Aluminum Oxide (LiAlO₂)								Al₁Li₁O₂(cr,l)

Enthalpy Reference Temperature = T_r = 298.15 K								Standard State Pressure = p° = 0.1 MPa
T/K		C_p^°		S^°		-[G^°-H^°(T_r)]/T		H-H^°(T_r)		_fH^°		_fG^°		log K_f
0		0.		0.		INFINITE		-9.693		-1180.523		-1180.523		INFINITE
100		17.966		8.046		99.257		-9.121		-1183.834		-1165.875		608.991
200		47.999		30.154		58.942		-5.758		-1187.025		-1146.565		299.452

298.15		67.777		53.313		53.313		0.		-1188.674		-1126.303		197.324

300		68.128		53.733		53.314		0.126		-1188.693		-1125.916		196.039
400		81.546		75.421		56.180		7.697		-1189.202		-1104.891		144.284
500		88.408		94.425		61.974		16.226		-1192.298		-1083.492		113.192

600		92.688		110.947		68.790		25.294		-1192.108		-1061.744		92.433
700		95.751		125.475		75.871		34.723		-1191.706		-1040.047		77.609
800		98.165		138.424		82.896		44.423		-1191.220		-1018.414		66.496
900		100.203		150.107		89.725		54.343		-1190.737		-996.843		57.855
1000		102.006		160.759		96.303		64.455		-1200.889		-974.563		50.906

1100		103.654		170.559		102.614		74.740		-1200.170		-951.964		45.205
1200		105.198		179.645		108.660		85.183		-1199.326		-929.436		40.457
1300		106.671		188.124		114.450		95.777		-1198.363		-906.983		36.443
1400		108.089		196.082		119.999		106.515		-1197.279		-884.609		33.005
1500		109.466		203.586		125.324		117.393		-1196.075		-862.317		30.029

1600		110.813		210.694		130.439		128.408		-1194.752		-840.109		27.427
1700		112.140		217.452		135.361		139.556		-1338.549		-810.812		24.913
1800		113.449		223.899		140.102		150.835		-1336.240		-779.835		22.630
1900		114.746		230.068		144.676		162.245		-1333.827		-748.988		20.591

1973.000		115.679		234.411		147.916		170.656		CRYSTAL <--> LIQUID
1973.000		125.520		278.945		147.916		258.520		TRANSITION

2000		125.520		280.651		149.696		261.909		-1243.184		-719.476		18.791

2100		125.520		286.775		156.079		274.461		-1239.679		-693.377		17.247
2200		125.520		292.614		162.154		287.013		-1236.201		-667.444		15.847
2300		125.520		298.194		167.948		299.565		-1232.750		-641.669		14.573
2400		125.520		303.536		173.487		312.117		-1229.327		-616.044		13.408
2500		125.520		308.660		178.792		324.669		-1225.934		-590.560		12.339

2600		125.520		313.583		183.882		337.221		-1222.571		-565.211		11.355
2700		125.520		318.320		188.774		349.773		-1219.240		-539.991		10.447
2800		125.520		322.885		193.483		362.325		-1509.843		-513.926		9.587
2900		125.520		327.289		198.021		374.877		-1505.483		-478.436		8.618
3000		125.520		331.545		202.402		387.429		-1501.159		-443.094		7.715

3100		125.520		335.660		206.634		399.981		-1496.871		-407.895		6.873
3200		125.520		339.646		210.729		412.533		-1492.621		-372.836		6.086
3300		125.520		343.508		214.694		425.085		-1488.408		-337.908		5.349
3400		125.520		347.255		218.538		437.637		-1484.235		-303.106		4.657
3500		125.520		350.894		222.268		450.189		-1480.104		-268.428		4.006

3600		125.520		354.430		225.891		462.741		-1476.013		-233.866		3.393
3700		125.520		357.869		229.411		475.293		-1471.966		-199.419		2.815
3800		125.520		361.216		232.836		487.845		-1467.963		-165.078		2.269
3900		125.520		364.477		236.170		500.397		-1464.005		-130.843		1.752
4000		125.520		367.654		239.417		512.949		-1460.094		-96.710		1.263

PREVIOUS:								CURRENT: December 1979

Lithium Aluminum Oxide (LiAlO₂)								Al₁Li₁O₂(cr,l)

Download table in tab-delimited text format.