		J·K^-1 mol^-1						kJ·mol^-1
Beryllium Aluminum Oxide (BeAl₆O₁₀)								Al₆Be₁O₁₀(l)

Enthalpy Reference Temperature = T_r = 298.15 K								Standard State Pressure = p° = 0.1 MPa
T/K		C_p^°		S^°		-[G^°-H^°(T_r)]/T		H-H^°(T_r)		_fH^°		_fG^°		log K_f
0
100
200

298.15		265.186		314.903		314.903		0.		-5299.312		-5033.981		881.933

300		266.546		316.548		314.908		0.492		-5299.391		-5032.335		876.207
400		324.268		401.832		326.143		30.275		-5301.355		-4942.905		645.477
500		358.527		478.189		349.073		64.558		-5300.266		-4853.375		507.029

600		380.560		545.629		376.328		101.581		-5297.720		-4764.221		414.762
700		396.083		605.518		404.873		140.452		-5294.599		-4675.547		348.894
800		407.827		659.205		433.367		180.671		-5291.446		-4587.329		299.522
900		417.249		707.802		461.203		221.939		-5288.643		-4499.488		261.143
1000		425.178		752.185		488.114		264.071		-5349.998		-4407.369		230.217

1100		431.998		793.036		514.002		306.937		-5346.498		-4313.271		204.820
1200		437.939		830.883		538.851		350.439		-5342.649		-4219.509		183.670
1300		443.295		866.151		562.687		394.503		-5338.496		-4126.080		165.788
1400		448.316		899.188		585.555		439.087		-5334.063		-4032.982		150.472

1400.010		448.316		899.191		585.557		439.091		GLASS <--> LIQUID
1400.010		569.024		899.191		585.557		439.091		TRANSITION

1500		569.024		938.446		607.787		495.988		-5317.538		-3940.627		137.225

1600		569.024		975.170		629.614		552.890		-5315.768		-3848.840		125.652
1700		569.024		1009.667		650.965		609.793		-5299.273		-3757.662		115.459
1800		569.024		1042.191		671.805		666.695		-5282.920		-3667.453		106.427
1900		569.024		1072.957		692.116		723.598		-5266.706		-3578.147		98.370
2000		569.024		1102.144		711.894		780.500		-5250.630		-3489.692		91.141

2100		569.024		1129.907		731.144		837.402		-5234.689		-3402.038		84.621

2186.000		569.024		1152.745		747.284		886.338		CRYSTAL <--> LIQUID

2200		569.024		1156.378		749.876		894.305		5218.884 3315.136 78.711
2300		569.024		1181.672		768.104		951.207		-5203.212		-3228.956		73.332
2400		569.024		1205.889		785.844		1008.110		-5187.674		-3143.454		68.415
2500		569.024		1229.118		803.113		1065.012		-5172.266		-3058.595		63.906

2600		569.024		1251.436		819.930		1121.914		-5156.987		-2974.350		59.755
2700		569.024		1272.911		836.312		1178.817		-5141.834		-2890.689		55.924
2800		569.024		1293.605		852.277		1235.719		-7181.169		-2795.558		52.152
2900		569.024		1313.573		867.841		1292.622		-7158.624		-2639.331		47.539
3000		569.024		1332.863		883.022		1349.524		-7136.183		-2483.875		43.248

3100		569.024		1351.522		897.836		1406.426		-7113.842		-2329.164		39.246
3200		569.024		1369.587		912.297		1463.329		-7091.601		-2175.178		35.506
3300		569.024		1387.097		926.421		1520.231		-7069.458		-2021.884		32.004
3400		569.024		1404.084		940.221		1577.134		-7047.412		-1869.255		28.718
3500		569.024		1420.579		953.711		1634.036		-7025.465		-1717.278		25.629

3600		569.024		1436.609		966.904		1690.938		-7003.614		-1565.924		22.721
3700		569.024		1452.199		979.810		1747.841		-6981.861		-1415.179		19.979
3800		569.024		1467.374		992.442		1804.743		-6960.207		-1265.014		17.389
3900		569.024		1482.155		1004.810		1861.646		-6938.652		-1115.420		14.939
4000		569.024		1496.561		1016.924		1918.548		-6917.201		-966.382		12.620

PREVIOUS:								CURRENT: June 1972

Beryllium Aluminum Oxide (BeAl₆O₁₀)								Al₆Be₁O₁₀(l)

Download table in tab-delimited text format.