Titanium Boride (TiB) B1Ti1(cr)
 
Enthalpy Reference Temperature = Tr = 298.15 K Standard State Pressure = p° = 0.1 MPa
  J·K-1 mol-1 kJ·mol-1  
T/K Cp° S° -[G°-H°(Tr)]/T H-H°(Tr) fH° fG° log Kf
0              
100              
200              
250              
 
298.15 29.673 34.727 34.727 0. -160.247 -159.691 27.977
 
300 29.916 34.911 34.728 0.055 -160.260 -159.687 27.804
400 40.334 45.065 36.041 3.610 -160.681 -159.420 20.818
500 45.714 54.690 38.824 7.933 -160.829 -159.085 16.620
 
600 48.568 63.297 42.200 12.658 -160.911 -158.729 13.819
700 50.124 70.910 45.769 17.599 -161.013 -158.358 11.817
800 50.911 77.657 49.341 22.652 -161.167 -157.968 10.314
900 51.488 83.688 52.829 27.774 -161.419 -157.555 9.144
1000 51.915 89.137 56.191 32.945 -161.831 -157.105 8.206
 
1100 52.191 94.099 59.415 38.152 -162.469 -156.604 7.436
1200 52.325 98.646 62.498 43.377 -167.327 -155.914 6.787
1300 52.459 102.839 65.442 48.617 -167.710 -154.948 6.226
1400 52.593 106.732 68.254 53.869 -168.206 -153.948 5.744
1500 52.727 110.365 70.941 59.135 -168.824 -152.909 5.325
 
1600 52.861 113.772 73.513 64.415 -169.576 -151.824 4.957
1700 52.995 116.981 75.976 69.707 -170.472 -150.688 4.630
1800 53.128 120.014 78.339 75.013 -171.524 -149.495 4.338
1900 53.262 122.890 80.609 80.333 -172.744 -148.239 4.075
2000 53.396 125.625 82.792 85.666 -188.831 -146.460 3.825
 
2100 53.530 128.233 84.894 91.012 -191.171 -144.284 3.589
2200 53.664 130.727 86.921 96.372 -193.532 -141.996 3.371
2300 53.798 133.115 88.878 101.745 -195.913 -139.600 3.170
2400 53.932 135.408 90.770 107.132 -248.574 -136.032 2.961
2500 54.066 137.612 92.599 112.531 -251.073 -131.291 2.743
 
2600 54.200 139.735 94.372 117.945 -253.558 -126.451 2.540
2700 54.333 141.783 96.090 123.371 -256.030 -121.515 2.351
2800 54.467 143.762 97.757 128.811 -258.489 -116.488 2.173
2900 54.601 145.675 99.377 134.265 -260.934 -111.373 2.006
3000 54.735 147.528 100.951 139.732 -263.366 -106.174 1.849
 
3100 54.869 149.325 102.483 145.212 -265.785 -100.895 1.700
3200 55.003 151.070 103.974 150.705 -268.190 -95.537 1.559
3300 55.137 152.764 105.427 156.212 -270.582 -90.105 1.426
3400 55.271 154.412 106.844 161.733 -272.960 -84.600 1.300
3500 55.405 156.016 108.226 167.267 -275.325 -79.026 1.179
 
3600 55.538 157.579 109.575 172.814 -277.677 -73.384 1.065
3700 55.672 159.102 110.893 178.374 -689.113 -59.888 0.845
3800 55.806 160.589 112.181 183.948 -690.204 -42.868 0.589
3900 55.940 162.040 113.441 189.535 -691.336 -25.818 0.346
4000 56.074 163.458 114.674 195.136 -692.509 -8.739 0.114
 
PREVIOUS: March 1963 CURRENT: June 1965
 
Titanium Boride (TiB) B1Ti1(cr)

Download table in tab-delimited text format.