Titanium Boride (TiB2) B2Ti1(cr)
 
Enthalpy Reference Temperature = Tr = 298.15 K Standard State Pressure = p° = 0.1 MPa
  J·K-1 mol-1 kJ·mol-1  
T/K Cp° S° -[G°-H°(Tr)]/T H-H°(Tr) fH° fG° log Kf
0 0. 0. INFINITE -5.577 -277.811 -277.811 INFINITE
100 7.523 2.518 56.366 -5.385 -278.227 -277.591 144.999
200 28.125 14.046 32.058 -3.602 -279.027 -276.623 72.247
 
298.15 44.279 28.485 28.485 0. -279.491 -275.334 48.237
 
300 44.522 28.759 28.486 0.082 -279.498 -275.308 47.935
400 54.890 43.136 30.375 5.104 -279.814 -273.864 35.763
500 61.668 56.156 34.253 10.952 -280.169 -272.336 28.451
 
600 66.166 67.815 38.893 17.353 -280.556 -270.734 23.569
700 69.496 78.274 43.785 24.142 -280.964 -269.064 20.078
800 72.069 87.723 48.696 31.222 -281.376 -267.336 17.455
900 74.534 96.355 53.519 38.553 -281.799 -265.556 15.412
1000 76.889 104.331 58.206 46.125 -282.273 -263.727 13.776
 
1100 79.136 111.765 62.741 53.927 -282.845 -261.846 12.434
1200 81.283 118.744 67.120 61.949 -287.496 -259.788 11.308
1300 83.320 125.331 71.347 70.180 -287.529 -257.477 10.346
1400 85.249 131.577 75.428 78.609 -287.537 -255.165 9.520
1500 87.069 137.521 79.371 87.226 -287.539 -252.853 8.805
 
1600 88.780 143.196 83.184 96.019 -287.553 -250.540 8.179
1700 90.383 148.627 86.875 104.978 -287.599 -248.225 7.627
1800 91.876 153.836 90.451 114.092 -287.698 -245.907 7.136
1900 93.261 158.841 93.920 123.350 -287.872 -243.581 6.696
2000 94.537 163.657 97.287 132.741 -302.828 -240.789 6.289
 
2100 95.705 168.298 100.558 142.254 -303.964 -237.659 5.911
2200 96.763 172.775 103.740 151.878 -305.057 -234.476 5.567
2300 97.713 177.098 106.836 161.603 -306.118 -231.244 5.252
2400 98.554 181.275 109.851 171.416 -407.675 -225.829 4.915
2500 99.391 185.315 112.789 181.314 -408.851 -218.227 4.560
 
2600 100.228 189.229 115.654 191.295 -409.944 -210.581 4.231
2700 101.065 193.028 118.450 201.359 -410.953 -202.893 3.925
2800 101.901 196.718 121.180 211.507 -411.879 -195.170 3.641
2900 102.738 200.309 123.847 221.739 -412.721 -187.415 3.376
3000 103.575 203.806 126.454 232.055 -413.479 -179.633 3.128
 
3100 104.412 207.215 129.004 242.454 -414.153 -171.827 2.895
 
3193.000 105.190 210.313 131.328 252.201 CRYSTAL <--> LIQUID
 
3200 105.249 210.544 131.501 252.937 414.744 164.000 2.677
3300 106.085 213.795 133.945 263.504 -415.251 -156.157 2.472
3400 106.922 216.975 136.341 274.154 -415.674 -148.299 2.278
3500 107.759 220.086 138.689 284.889 -416.014 -140.429 2.096
 
3600 108.596 223.133 140.993 295.706 -416.270 -132.552 1.923
3700 109.433 226.120 143.253 306.608 -825.541 -116.880 1.650
3800 110.269 229.050 145.473 317.593 -824.395 -97.742 1.344
3900 111.106 231.925 147.653 328.662 -823.221 -78.635 1.053
4000 111.943 234.748 149.795 339.814 -822.017 -59.558 0.778
 
PREVIOUS: December 1962 CURRENT: June 1965
 
Titanium Boride (TiB2) B2Ti1(cr)

Download table in tab-delimited text format.