fH°fG°| Lithium Tetrafluoroberyllate (Li2BeF4) | Be1F4Li2(l) | |||||||||||||
| Enthalpy Reference Temperature = Tr = 298.15 K | Standard State Pressure = p° = 0.1 MPa | |||||||||||||
| J·K-1 mol-1 | kJ·mol-1 | |||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| T/K | Cp° | S° | -[G°-H°(Tr)]/T | H-H°(Tr) | fH° |
fG° |
log Kf | |||||||
| 0 | ||||||||||||||
| 100 | ||||||||||||||
| 200 | ||||||||||||||
| 298.15 | 135.269 | 171.395 | 171.395 | 0. | -2241.068 | -2151.088 | 376.862 | |||||||
| 300 | 135.520 | 172.232 | 171.397 | 0.250 | -2241.055 | -2150.530 | 374.441 | |||||||
| 400 | 150.457 | 213.265 | 176.891 | 14.550 | -2240.238 | -2120.472 | 276.905 | |||||||
| 500 | 165.352 | 248.440 | 187.759 | 30.340 | -2245.147 | -2090.036 | 218.345 | |||||||
| 500.001 | 165.352 | 248.440 | 187.759 | 30.341 | GLASS <--> LIQUID | |||||||||
| + | ||||||||||||||
| 500.001 | 232.086 | 248.440 | 187.759 | 30.341 | TRANSITION | |||||||||
| 600 | 232.086 | 290.754 | 201.506 | 53.549 | -2237.119 | -2059.771 | 179.319 | |||||||
| 700 | 232.086 | 326.530 | 216.877 | 76.758 | -2229.255 | -2030.837 | 151.543 | |||||||
| 732.200 | 232.086 | 336.968 | 221.930 | 84.231 | CRYSTAL <--> LIQUID | |||||||||
| 800 | 232.086 | 357.521 | 232.563 | 99.966 | 2221.555 2003.019 130.784 | |||||||||
| 900 | 232.086 | 384.857 | 247.996 | 123.175 | -2214.029 | -1976.156 | 114.693 | |||||||
| 1000 | 232.086 | 409.310 | 262.926 | 146.384 | -2206.655 | -1950.122 | 101.864 | |||||||
| 1100 | 232.086 | 431.430 | 277.255 | 169.592 | -2199.420 | -1924.820 | 91.402 | |||||||
| 1200 | 232.086 | 451.624 | 290.957 | 192.801 | -2192.313 | -1900.171 | 82.712 | |||||||
| 1300 | 232.086 | 470.201 | 304.040 | 216.010 | -2185.333 | -1876.110 | 75.383 | |||||||
| 1400 | 232.086 | 487.400 | 316.530 | 239.218 | -2178.470 | -1852.582 | 69.121 | |||||||
| 1500 | 232.086 | 503.413 | 328.461 | 262.427 | -2171.718 | -1829.540 | 63.710 | |||||||
| 1600 | 232.086 | 518.391 | 339.869 | 285.635 | -2179.611 | -1806.420 | 58.974 | |||||||
| 1700 | 232.086 | 532.461 | 350.788 | 308.844 | -2463.146 | -1768.956 | 54.353 | |||||||
| 1800 | 232.086 | 545.727 | 361.253 | 332.053 | -2454.737 | -1728.364 | 50.156 | |||||||
| 1900 | 232.086 | 558.275 | 371.296 | 355.261 | -2446.377 | -1688.238 | 46.413 | |||||||
| 2000 | 232.086 | 570.180 | 380.945 | 378.470 | -2438.061 | -1648.551 | 43.056 | |||||||
| 2100 | 232.086 | 581.503 | 390.228 | 401.679 | -2429.783 | -1609.280 | 40.029 | |||||||
| 2200 | 232.086 | 592.300 | 399.169 | 424.887 | -2421.540 | -1570.402 | 37.286 | |||||||
| 2300 | 232.086 | 602.617 | 407.792 | 448.096 | -2413.325 | -1531.897 | 34.790 | |||||||
| 2400 | 232.086 | 612.494 | 416.117 | 471.305 | -2405.134 | -1493.750 | 32.511 | |||||||
| 2500 | 232.086 | 621.968 | 424.163 | 494.513 | -2396.963 | -1455.944 | 30.420 | |||||||
| PREVIOUS: June 1966 | CURRENT: December 1971 | |||||||||||||
| Lithium Tetrafluoroberyllate (Li2BeF4) | Be1F4Li2(l) | |||||||||||||
Download table in tab-delimited text format.