Beryllium Carbide (Be2C)								C1Be2(l)
Enthalpy Reference Temperature = Tr = 298.15 K								Standard State Pressure = p° = 0.1 MPa
		J·K-1 mol-1						kJ·mol-1
T/K		Cp°		S°		-[G°-H°(Tr)]/T		H-H°(Tr)		fH°		fG°		log Kf
0
100
200
298.15		43.250		47.467		47.467		0.		-15.893		-22.704		3.978
300		43.329		47.735		47.468		0.080		-15.889		-22.747		3.961
400		47.614		60.838		49.225		4.645		-16.031		-25.027		3.268
500		49.752		71.692		52.665		9.513		-16.694		-27.209		2.843
600		51.890		80.855		56.618		14.542		-17.778		-29.215		2.543
700		60.434		89.550		60.702		20.194		-18.682		-31.043		2.316
800		64.706		97.899		64.835		26.451		-19.340		-32.763		2.139
900		68.977		105.767		68.950		33.135		-19.875		-34.407		1.997
1000		73.249		113.255		73.009		40.246		-20.253		-36.000		1.880
1100		77.525		120.437		76.996		47.785		-20.450		-37.564		1.784
1200		81.797		127.374		80.907		55.760		-20.443		-39.118		1.703
1300		85.011		134.054		84.740		64.108		-20.284		-40.680		1.635
1400		87.278		140.441		88.492		72.728		-20.068		-42.257		1.577
1500		88.881		146.520		92.160		81.540		-19.872		-43.849		1.527
1600		90.023		152.295		95.739		90.489		-48.819		-44.401		1.450
1600.000		90.023		152.295		95.739		90.489		GLASS <--> LIQUID
1600.000		92.048		152.295		95.739		90.489		TRANSITION
1700		92.048		157.876		99.232		99.694		-47.843		-44.155		1.357
1800		92.048		163.137		102.638		108.899		-46.934		-43.965		1.276
1900		92.048		168.114		105.954		118.104		-46.090		-43.823		1.205
2000		92.048		172.835		109.181		127.308		-45.310		-43.724		1.142
2100		92.048		177.326		112.320		136.513		-44.592		-43.663		1.086
2200		92.048		181.608		115.373		145.718		-43.936		-43.634		1.036
2300		92.048		185.700		118.342		154.923		-43.339		-43.634		0.991
2400		92.048		189.617		121.231		164.128		-42.801		-43.659		0.950
2400.000		92.048		189.617		121.231		164.128		CRYSTAL <--> LIQUID
2500		92.048		193.375		124.042		173.332		42.321 43.705 0.913
2600		92.048		196.985		126.779		182.537		-41.900		-43.769		0.879
2700		92.048		200.459		129.444		191.742		-41.535		-43.848		0.848
2800		92.048		203.807		132.040		200.947		-623.142		-31.494		0.588
2900		92.048		207.037		134.571		210.152		-620.764		-10.406		0.187
3000		92.048		210.157		137.039		219.356		-618.409		10.601		-0.185
3100		92.048		213.176		139.446		228.561		-616.080		31.529		-0.531
3200		92.048		216.098		141.796		237.766		-613.778		52.383		-0.855
3300		92.048		218.930		144.091		246.971		-611.507		73.166		-1.158
3400		92.048		221.678		146.333		256.176		-609.270		93.880		-1.442
3500		92.048		224.347		148.524		265.380		-607.070		114.528		-1.709
PREVIOUS: March 1962								CURRENT: June 1963
Beryllium Carbide (Be2C)								C1Be2(l)

Download table in tab-delimited text format.