Silicon Carbide, Beta (SiC)								C1Si1(cr)
Enthalpy Reference Temperature = Tr = 298.15 K								Standard State Pressure = p° = 0.1 MPa
		J·K-1 mol-1						kJ·mol-1
T/K		Cp°		S°		-[G°-H°(Tr)]/T		H-H°(Tr)		fH°		fG°		log Kf
0		0.		0.		INFINITE		-3.270		-72.221		-72.221		INFINITE
100		4.263		1.460		33.062		-3.160		-72.437		-72.104		37.664
200		16.301		8.033		18.740		-2.141		-72.923		-71.580		18.695
298.15		26.840		16.610		16.610		0.		-73.220		-70.850		12.413
300		27.008		16.777		16.611		0.050		-73.223		-70.835		12.333
400		34.100		25.598		17.765		3.133		-73.284		-70.025		9.144
500		38.639		33.727		20.158		6.784		-73.237		-69.215		7.231
600		41.790		41.066		23.042		10.814		-73.161		-68.417		5.956
700		44.108		47.690		26.098		15.115		-73.082		-67.633		5.047
800		45.878		53.700		29.178		19.618		-73.009		-66.859		4.365
900		47.283		59.188		32.212		24.278		-72.945		-66.094		3.836
1000		48.421		64.231		35.165		29.065		-72.892		-65.336		3.413
1100		49.363		68.891		38.022		33.956		-72.851		-64.583		3.067
1200		50.158		73.221		40.777		38.932		-72.824		-63.832		2.779
1300		50.840		77.263		43.430		43.983		-72.813		-63.084		2.535
1400		51.430		81.053		45.984		49.097		-72.821		-62.335		2.326
1500		51.944		84.619		48.442		54.266		-72.851		-61.585		2.145
1600		52.400		87.986		50.809		59.484		-72.904		-60.832		1.986
1700		52.806		91.176		53.090		64.745		-123.160		-59.629		1.832
1800		53.170		94.204		55.291		70.044		-123.038		-55.895		1.622
1900		53.497		97.088		57.416		75.377		-122.903		-52.169		1.434
2000		53.798		99.840		59.469		80.742		-122.757		-48.450		1.265
2100		54.070		102.471		61.454		86.136		-122.601		-44.738		1.113
2200		54.321		104.992		63.376		91.556		-122.438		-41.034		0.974
2300		54.555		107.412		65.239		97.000		-122.267		-37.338		0.848
2400		54.769		109.739		67.045		102.466		-122.090		-33.649		0.732
2500		54.965		111.979		68.797		107.953		-121.908		-29.967		0.626
2600		55.153		114.138		70.500		113.459		-121.722		-26.294		0.528
2700		55.329		116.223		72.155		118.983		-121.531		-22.627		0.438
2800		55.492		118.238		73.765		124.524		-121.338		-18.967		0.354
2900		55.643		120.188		75.332		130.081		-121.142		-15.315		0.276
3000		55.789		122.077		76.859		135.653		-120.944		-11.669		0.203
3100		55.928		123.908		78.348		141.239		-120.746		-8.030		0.135
3200		56.057		125.686		79.799		146.838		-120.546		-4.397		0.072
3300		56.183		127.413		81.216		152.450		-120.346		-0.770		0.012
3400		56.300		129.092		82.600		158.074		-120.146		2.850		-0.044
3500		56.413		130.726		83.951		163.710		-119.946		6.465		-0.096
3600		56.522		132.316		85.273		169.357		-503.899		20.535		-0.298
3700		56.626		133.866		86.565		175.014		-503.288		35.094		-0.495
3800		56.722		135.378		87.830		180.681		-502.679		49.637		-0.682
3900		56.819		136.853		89.068		186.359		-502.074		64.163		-0.859
4000		56.911		138.292		90.281		192.045		-501.472		78.675		-1.027
PREVIOUS:								CURRENT: March 1967
Silicon Carbide, Beta (SiC)								C1Si1(cr)