Titanium Carbide (TiC) C1Ti1(cr)
 
Enthalpy Reference Temperature = Tr = 298.15 K Standard State Pressure = p° = 0.1 MPa
  J·K-1 mol-1 kJ·mol-1  
T/K Cp° S° -[G°-H°(Tr)]/T H-H°(Tr) fH° fG° log Kf
0 0. 0. INFINITE -4.607 -182.822 -182.822 INFINITE
100 7.335 2.602 46.702 -4.410 -183.245 -182.584 95.372
200 14.924 12.780 27.026 -2.849 -183.928 -181.622 47.435
 
298.15 33.807 24.229 24.229 0. -184.096 -180.438 31.612
 
300 33.936 24.439 24.230 0.063 -184.096 -180.415 31.413
400 40.685 35.180 25.648 3.813 -183.982 -179.200 23.401
500 45.166 44.777 28.533 8.122 -183.740 -178.031 18.599
 
600 47.647 53.248 31.962 12.772 -183.494 -176.913 15.402
700 49.032 60.703 35.546 17.610 -183.316 -175.831 13.121
800 49.903 67.310 39.112 22.558 -183.214 -174.770 11.411
900 50.572 73.227 42.579 27.583 -183.215 -173.715 10.082
1000 51.179 78.586 45.916 32.670 -183.372 -172.653 9.018
 
1100 51.794 83.493 49.112 37.818 -183.732 -171.566 8.147
1200 52.446 88.027 52.169 43.030 -188.267 -170.317 7.414
1300 53.145 92.252 55.091 48.309 -188.267 -168.821 6.783
1400 53.894 96.218 57.889 53.661 -188.314 -167.324 6.243
1500 54.689 99.963 60.570 59.090 -188.410 -165.821 5.774
 
1600 55.530 103.519 63.144 64.600 -188.559 -164.311 5.364
1700 56.404 106.912 65.620 70.197 -188.767 -162.789 5.002
1800 57.317 110.161 68.005 75.882 -189.042 -161.254 4.679
1900 58.254 113.285 70.306 81.661 -189.390 -159.701 4.390
2000 59.220 116.298 72.531 87.534 -204.508 -157.674 4.118
 
2100 60.208 119.211 74.685 93.506 -205.780 -155.301 3.863
2200 61.216 122.035 76.773 99.577 -206.969 -152.869 3.630
2300 62.241 124.779 78.801 105.749 -208.073 -150.384 3.415
2400 63.283 127.450 80.773 112.025 -209.091 -147.854 3.218
2500 64.337 130.054 82.692 118.406 -210.019 -145.283 3.036
 
2600 65.400 132.598 84.563 124.893 -210.856 -142.677 2.866
2700 66.480 135.087 86.388 131.487 -211.600 -140.040 2.709
2800 67.563 137.524 88.171 138.189 -212.249 -137.378 2.563
2900 68.659 139.914 89.914 145.000 -212.803 -134.694 2.426
3000 69.760 142.260 91.620 151.921 -213.261 -131.992 2.298
 
3100 70.869 144.566 93.291 158.952 -213.621 -129.277 2.178
3200 71.982 146.833 94.929 166.095 -213.882 -126.552 2.066
 
3290.000 72.987 148.844 96.376 172.618 CRYSTAL <--> LIQUID
 
3300 73.101 149.066 96.536 173.349 214.044 123.820 1.960
3400 74.224 151.264 98.113 180.715 -214.106 -121.085 1.860
3500 75.353 153.432 99.663 188.194 -214.068 -118.349 1.766
 
3600 76.485 155.571 101.186 195.786 -213.928 -115.616 1.678
3700 77.621 157.682 102.684 203.491 -622.785 -105.100 1.484
3800 78.760 159.767 104.159 211.310 -621.207 -91.129 1.253
3900 79.902 161.828 105.612 219.243 -619.582 -77.201 1.034
4000 81.048 163.865 107.042 227.291 -617.908 -63.315 0.827
 