Titanium Carbide (TiC)								C1Ti1(l)
Enthalpy Reference Temperature = Tr = 298.15 K								Standard State Pressure = p° = 0.1 MPa
		J·K-1 mol-1						kJ·mol-1
T/K		Cp°		S°		-[G°-H°(Tr)]/T		H-H°(Tr)		fH°		fG°		log Kf
0
100
200
298.15		33.807		47.401		47.401		0.		-108.334		-111.585		19.549
300		33.936		47.610		47.401		0.063		-108.334		-111.605		19.432
400		40.685		58.352		48.820		3.813		-108.221		-112.707		14.718
500		45.166		67.949		51.705		8.122		-107.978		-113.855		11.894
600		47.647		76.420		55.133		12.772		-107.732		-115.054		10.016
700		49.032		83.875		58.718		17.610		-107.555		-116.290		8.678
800		49.903		90.481		62.283		22.558		-107.452		-117.545		7.675
900		50.572		96.398		65.751		27.583		-107.454		-118.808		6.895
1000		51.179		101.758		69.088		32.670		-107.610		-120.063		6.271
1100		51.794		106.664		72.284		37.818		-107.971		-121.293		5.760
1200		52.446		111.199		75.340		43.030		-112.505		-122.361		5.326
1300		53.145		115.424		78.263		48.309		-112.506		-123.183		4.950
1400		53.894		119.389		81.060		53.661		-112.552		-124.002		4.627
1500		54.689		123.135		83.742		59.090		-112.648		-124.817		4.347
1600		55.530		126.691		86.316		64.600		-112.797		-125.624		4.101
1700		56.404		130.083		88.791		70.197		-113.006		-126.420		3.884
1800		57.317		133.333		91.176		75.882		-113.280		-127.201		3.691
1900		58.254		136.457		93.478		81.661		-113.629		-127.965		3.518
2000		59.220		139.470		95.702		87.534		-128.747		-128.256		3.350
2100		60.208		142.383		97.856		93.506		-130.018		-128.199		3.189
2200		61.216		145.207		99.945		99.577		-131.207		-128.085		3.041
2200.000		61.216		145.207		99.945		99.577		GLASS <--> LIQUID
2200.000		62.760		145.207		99.945		99.577		TRANSITION
2300		62.760		147.997		101.974		105.853		-132.209		-127.920		2.905
2400		62.760		150.668		103.947		112.129		-133.226		-127.712		2.780
2500		62.760		153.230		105.868		118.405		-134.259		-127.461		2.663
2600		62.760		155.691		107.737		124.681		-135.307		-127.169		2.555
2700		62.760		158.060		109.557		130.957		-136.369		-126.835		2.454
2800		62.760		160.342		111.330		137.233		-137.444		-126.463		2.359
2900		62.760		162.544		113.059		143.509		-138.534		-126.051		2.270
3000		62.760		164.672		114.744		149.785		-139.636		-125.602		2.187
3100		62.760		166.730		116.388		156.061		-140.751		-125.116		2.108
3200		62.760		168.723		117.992		162.337		-141.879		-124.594		2.034
3290.000		62.760		170.463		119.404		167.985		CRYSTAL <--> LIQUID
3300		62.760		170.654		119.559		168.613		143.019 124.036 1.963
3400		62.760		172.527		121.089		174.889		-144.171		-123.443		1.896
3500		62.760		174.347		122.585		181.165		-145.336		-122.817		1.833
3600		62.760		176.115		124.048		187.441		-146.512		-122.157		1.772
3700		62.760		177.834		125.478		193.717		-556.798		-113.676		1.605
3800		62.760		179.508		126.878		199.993		-556.763		-101.700		1.398
3900		62.760		181.138		128.249		206.269		-556.795		-89.724		1.202
4000		62.760		182.727		129.591		212.545		-556.892		-77.747		1.015
4100		62.760		184.277		130.906		218.821		-557.053		-65.767		0.838
4200		62.760		185.789		132.195		225.097		-557.277		-53.781		0.669
4300		62.760		187.266		133.458		231.373		-557.560		-41.790		0.508
4400		62.760		188.709		134.698		237.649		-557.902		-29.792		0.354
4500		62.760		190.119		135.914		243.925		-558.301		-17.785		0.206