Titanium Carbide (TiC) C1Ti1(cr,l)
 
Enthalpy Reference Temperature = Tr = 298.15 K Standard State Pressure = p° = 0.1 MPa
  J·K-1 mol-1 kJ·mol-1  
T/K Cp° S° -[G°-H°(Tr)]/T H-H°(Tr) fH° fG° log Kf
0 0. 0. INFINITE -4.607 -182.822 -182.822 INFINITE
100 7.335 2.602 46.702 -4.410 -183.245 -182.584 95.372
200 14.924 12.780 27.026 -2.849 -183.928 -181.622 47.435
 
298.15 33.807 24.229 24.229 0. -184.096 -180.438 31.612
 
300 33.936 24.439 24.230 0.063 -184.096 -180.415 31.413
400 40.685 35.180 25.648 3.813 -183.982 -179.200 23.401
500 45.166 44.777 28.533 8.122 -183.740 -178.031 18.599
 
600 47.647 53.248 31.962 12.772 -183.494 -176.913 15.402
700 49.032 60.703 35.546 17.610 -183.316 -175.831 13.121
800 49.903 67.310 39.112 22.558 -183.214 -174.770 11.411
900 50.572 73.227 42.579 27.583 -183.215 -173.715 10.082
1000 51.179 78.586 45.916 32.670 -183.372 -172.653 9.018
 
1100 51.794 83.493 49.112 37.818 -183.732 -171.566 8.147
1200 52.446 88.027 52.169 43.030 -188.267 -170.317 7.414
1300 53.145 92.252 55.091 48.309 -188.267 -168.821 6.783
1400 53.894 96.218 57.889 53.661 -188.314 -167.324 6.243
1500 54.689 99.963 60.570 59.090 -188.410 -165.821 5.774
 
1600 55.530 103.519 63.144 64.600 -188.559 -164.311 5.364
1700 56.404 106.912 65.620 70.197 -188.767 -162.789 5.002
1800 57.317 110.161 68.005 75.882 -189.042 -161.254 4.679
1900 58.254 113.285 70.306 81.661 -189.390 -159.701 4.390
2000 59.220 116.298 72.531 87.534 -204.508 -157.674 4.118
 
2100 60.208 119.211 74.685 93.506 -205.780 -155.301 3.863
2200 61.216 122.035 76.773 99.577 -206.969 -152.869 3.630
2300 62.241 124.779 78.801 105.749 -208.073 -150.384 3.415
2400 63.283 127.450 80.773 112.025 -209.091 -147.854 3.218
2500 64.337 130.054 82.692 118.406 -210.019 -145.283 3.036
 
2600 65.400 132.598 84.563 124.893 -210.856 -142.677 2.866
2700 66.480 135.087 86.388 131.487 -211.600 -140.040 2.709
2800 67.563 137.524 88.171 138.189 -212.249 -137.378 2.563
2900 68.659 139.914 89.914 145.000 -212.803 -134.694 2.426
3000 69.760 142.260 91.620 151.921 -213.261 -131.992 2.298
 
3100 70.869 144.566 93.291 158.952 -213.621 -129.277 2.178
3200 71.982 146.833 94.929 166.095 -213.882 -126.552 2.066
 
3290.000 72.987 148.844 96.376 172.618 CRYSTAL <--> LIQUID
3290.000 62.760 170.463 96.376 243.746 TRANSITION
 
3300 62.760 170.654 96.601 244.374 -143.019 -124.036 1.963
3400 62.760 172.527 98.807 250.650 -144.171 -123.443 1.896
3500 62.760 174.347 100.939 256.926 -145.336 -122.817 1.833
 
3600 62.760 176.115 103.003 263.202 -146.512 -122.157 1.772
3700 62.760 177.834 105.002 269.478 -556.798 -113.676 1.605
3800 62.760 179.508 106.941 275.754 -556.763 -101.700 1.398
3900 62.760 181.138 108.823 282.030 -556.795 -89.724 1.202
4000 62.760 182.727 110.650 288.306 -556.892 -77.747 1.015
 
4100 62.760 184.277 112.427 294.582 -557.053 -65.767 0.838
4200 62.760 185.789 114.156 300.858 -557.277 -53.781 0.669
4300 62.760 187.266 115.839 307.134 -557.560 -41.790 0.508
4400 62.760 188.709 117.479 313.410 -557.902 -29.792 0.354
4500 62.760 190.119 119.078 319.686 -558.301 -17.785 0.206
 
PREVIOUS: CURRENT: June 1968
 
Titanium Carbide (TiC) C1Ti1(cr,l)

Download table in tab-delimited text format.