Calcium Oxide (CaO)								Ca1O1(l)
Enthalpy Reference Temperature = Tr = 298.15 K								Standard State Pressure = p° = 0.1 MPa
		J·K-1 mol-1						kJ·mol-1
T/K		Cp°		S°		-[G°-H°(Tr)]/T		H-H°(Tr)		fH°		fG°		log Kf
0
100
200
298.15		42.120		62.321		62.321		0.		-557.335		-532.935		93.368
300		42.242		62.582		62.322		0.078		-557.332		-532.783		92.766
400		46.626		75.409		64.041		4.547		-556.984		-524.644		68.511
500		48.982		86.089		67.413		9.338		-556.488		-516.616		53.971
600		50.480		95.160		71.301		14.315		-556.033		-508.686		44.285
700		51.555		103.026		75.284		19.419		-555.695		-500.823		37.372
800		52.400		109.966		79.194		24.618		-556.358		-492.895		32.183
900		53.112		116.180		82.964		29.894		-556.310		-484.968		28.147
1000		53.735		121.809		86.572		35.237		-556.519		-477.032		24.918
1100		54.300		126.957		90.012		40.639		-556.995		-469.062		22.274
1200		54.831		131.705		93.291		46.096		-565.472		-460.415		20.041
1300		55.329		136.114		96.418		51.604		-565.255		-451.669		18.148
1400		55.810		140.232		99.402		57.161		-565.005		-442.941		16.526
1500		56.275		144.098		102.254		62.766		-564.721		-434.232		15.121
1600		56.727		147.744		104.984		68.416		-564.405		-425.543		13.893
1700		57.174		151.197		107.602		74.111		-564.056		-416.874		12.809
1800		57.609		154.477		110.116		79.850		-712.348		-406.017		11.782
1900		58.045		157.604		112.534		85.633		-710.521		-389.048		10.696
2000		58.471		160.592		114.862		91.459		-708.669		-372.176		9.720
2100		58.894		163.455		117.109		97.327		-706.793		-355.397		8.840
2100.000		58.894		163.455		117.109		97.327		GLASS <--> LIQUID
+
2100.000		62.760		163.455		117.109		97.327		TRANSITION
2200		62.760		166.374		119.282		103.603		-704.531		-338.717		8.042
2300		62.760		169.164		121.391		109.879		-702.296		-322.140		7.316
2400		62.760		171.835		123.437		116.155		-700.092		-305.659		6.652
2500		62.760		174.397		125.425		122.431		-697.922		-289.269		6.044
2600		62.760		176.859		127.356		128.707		-695.794		-272.965		5.484
2700		62.760		179.227		129.234		134.983		-693.714		-256.741		4.967
2800		62.760		181.510		131.060		141.259		-691.688		-240.594		4.488
2900		62.760		183.712		132.838		147.535		-689.724		-224.519		4.044
3000		62.760		185.840		134.569		153.811		-687.829		-208.510		3.630
3100		62.760		187.898		136.257		160.087		-686.011		-192.562		3.245
3200		62.760		189.890		137.902		166.363		-684.278		-176.673		2.884
3200.000		62.760		189.890		137.902		166.363		CRYSTAL <--> LIQUID
3300		62.760		191.821		139.507		172.639		682.638 160.836 2.546
3400		62.760		193.695		141.073		178.915		-681.099		-145.047		2.228
3500		62.760		195.514		142.603		185.191		-679.668		-129.302		1.930
3600		62.760		197.282		144.097		191.467		-678.352		-113.596		1.648
3700		62.760		199.002		145.558		197.743		-677.158		-97.925		1.382
3800		62.760		200.676		146.986		204.019		-676.092		-82.285		1.131
3900		62.760		202.306		148.384		210.295		-675.160		-66.670		0.893
4000		62.760		203.895		149.752		216.571		-674.364		-51.079		0.667
4100		62.760		205.444		151.091		222.847		-673.711		-35.505		0.452
4200		62.760		206.957		152.404		229.123		-673.202		-19.946		0.248
4300		62.760		208.434		153.690		235.399		-672.840		-4.396		0.053
4400		62.760		209.876		154.950		241.675		-672.622		11.146		-0.132
4500		62.760		211.287		156.187		247.951		-672.538		26.683		-0.310