Chromium (Cr) Cr1(l) T(K) Cp S -[G-H(Tr)]/T H-H(Tr) delta-f H delta-f G log Kf 0 100 200 250 298.15 23.434 36.205 36.205 0. 26.068 22.316 -3.910 300 23.472 36.350 36.205 0.043 26.068 22.292 -3.881 350 24.393 40.036 36.495 1.240 26.067 21.663 -3.233 400 25.230 43.349 37.148 2.481 26.067 21.034 -2.747 450 25.983 46.365 38.007 3.761 26.067 20.405 -2.369 500 26.631 49.137 38.983 5.077 26.067 19.775 -2.066 600 27.722 54.092 41.098 7.797 26.068 18.517 -1.612 700 28.577 58.430 43.271 10.611 26.068 17.259 -1.288 800 29.434 62.299 45.412 13.510 26.068 16.000 -1.045 900 30.501 65.825 47.487 16.505 26.068 14.742 -0.856 1000 31.861 69.107 49.486 19.621 26.068 13.483 -0.704 1100 33.472 72.218 51.412 22.886 26.068 12.225 -0.581 1200 35.187 75.203 53.271 26.318 26.068 10.967 -0.477 1300 37.116 78.095 55.070 29.932 26.068 9.708 -0.390 1350.000 38.112 79.514 55.949 31.813 GLASS <--> LIQUID 1350.000 39.330 79.514 55.949 31.813 TRANSITION 1400 39.330 80.944 56.816 33.779 26.103 8.449 -0.315 1500 39.330 83.658 58.516 37.712 26.020 7.190 -0.250 1600 39.330 86.196 60.168 41.645 25.727 5.943 -0.194 1700 39.330 88.581 61.770 45.578 25.219 4.720 -0.145 1800 39.330 90.829 63.322 49.511 24.492 3.535 -0.103 1900 39.330 92.955 64.827 53.444 23.542 2.395 -0.066 2000 39.330 94.972 66.284 57.377 22.368 1.311 -0.034 2100 39.330 96.891 67.696 61.310 20.967 0.292 -0.007 2130.000 39.330 97.449 68.111 62.490 CRYSTAL <--> LIQUID 2200 39.330 98.721 69.065 65.243 0. 0. 0. 2300 39.330 100.469 70.393 69.176 0. 0. 0. 2400 39.330 102.143 71.681 73.109 0. 0. 0. 2500 39.330 103.749 72.932 77.042 0. 0. 0. 2600 39.330 105.291 74.147 80.975 0. 0. 0. 2700 39.330 106.775 75.328 84.908 0. 0. 0. 2800 39.330 108.206 76.477 88.841 0. 0. 0. 2900 39.330 109.586 77.595 92.774 0. 0. 0. 2952.078 39.330 110.286 78.165 94.822 FUGACITY = 1 bar 3000 39.330 110.919 78.684 96.707 339.122 5.508 0.096 3100 39.330 112.209 79.744 100.640 -338.294 16.982 -0.286 3200 39.330 113.457 80.779 104.572 -337.516 28.430 -0.464 3300 39.330 114.668 81.787 108.505 -336.786 39.855 -0.631 3400 39.330 115.842 82.772 112.438 -336.104 51.258 -0.787 3500 39.330 116.982 83.733 116.371 -335.469 62.641 -0.935