Copper (Cu)								Cu1(l)
Enthalpy Reference Temperature = Tr = 298.15 K								Standard State Pressure = p° = 0.1 MPa
		J·K-1 mol-1						kJ·mol-1
T/K		Cp°		S°		-[G°-H°(Tr)]/T		H-H°(Tr)		fH°		fG°		log Kf
0
100
200
298.15		24.442		41.620		41.620		0.		11.857		9.336		-1.636
300		24.460		41.772		41.621		0.045		11.857		9.320		-1.623
350		24.973		45.583		41.921		1.282		11.857		8.898		-1.328
400		25.316		48.939		42.592		2.539		11.857		8.475		-1.107
450		25.684		51.944		43.467		3.814		11.857		8.052		-0.935
500		25.910		54.661		44.453		5.104		11.857		7.629		-0.797
600		26.478		59.436		46.563		7.724		11.857		6.784		-0.591
700		26.993		63.557		48.703		10.398		11.856		5.938		-0.443
800		27.491		67.193		50.791		13.121		11.856		5.093		-0.333
900		28.047		70.463		52.798		15.898		11.856		4.248		-0.247
900.000		28.047		70.463		52.798		15.898		GLASS <--> LIQUID
900.000		32.844		70.463		52.798		15.898		TRANSITION
1000		32.844		73.923		54.741		19.182		12.306		3.378		-0.176
1100		32.844		77.053		56.629		22.467		12.686		2.466		-0.117
1200		32.844		79.911		58.452		25.751		12.975		1.523		-0.066
1300		32.844		82.540		60.205		29.036		13.131		0.561		-0.023
1358.000		32.844		83.974		61.190		30.941		CRYSTAL <--> LIQUID
1400		32.844		84.974		61.889		32.320		0. 0. 0.
1500		32.844		87.240		63.504		35.604		0.		0.		0.
1600		32.844		89.360		65.055		38.889		0.		0.		0.
1700		32.844		91.351		66.543		42.173		0.		0.		0.
1800		32.844		93.229		67.974		45.458		0.		0.		0.
1900		32.844		95.004		69.351		48.742		0.		0.		0.
2000		32.844		96.689		70.676		52.027		0.		0.		0.
2100		32.844		98.292		71.953		55.311		0.		0.		0.
2200		32.844		99.819		73.185		58.596		0.		0.		0.
2300		32.844		101.279		74.375		61.880		0.		0.		0.
2400		32.844		102.677		75.525		65.164		0.		0.		0.
2500		32.844		104.018		76.639		68.449		0.		0.		0.
2600		32.844		105.306		77.717		71.733		0.		0.		0.
2700		32.844		106.546		78.761		75.018		0.		0.		0.
2800		32.844		107.740		79.775		78.302		0.		0.		0.
2843.261		32.844		108.244		80.205		79.723		FUGACITY = 1 bar
2900		32.844		108.893		80.760		81.587		300.204 5.996 0.108
3000		32.844		110.006		81.716		84.871		-299.409		16.541		-0.288
3100		32.844		111.083		82.646		88.155		-298.665		27.060		-0.456
3200		32.844		112.126		83.551		91.440		-297.971		37.556		-0.613
3300		32.844		113.137		84.432		94.724		-297.328		48.031		-0.760
3400		32.844		114.117		85.291		98.009		-296.737		58.488		-0.899
3500		32.844		115.069		86.128		101.293		-296.195		68.927		-1.029
3600		32.844		115.995		86.945		104.578		-295.703		79.352		-1.151
3700		32.844		116.894		87.743		107.862		-295.259		89.764		-1.267
3800		32.844		117.770		88.521		111.147		-294.862		100.165		-1.377
3900		32.844		118.624		89.282		114.431		-294.509		110.556		-1.481
4000		32.844		119.455		90.026		117.715		-294.199		120.938		-1.579
PREVIOUS: December 1966								CURRENT: June 1977
Copper (Cu)								Cu1(l)

Download table in tab-delimited text format.