Copper (Cu)								Cu1(cr,l)
Enthalpy Reference Temperature = Tr = 298.15 K								Standard State Pressure = p° = 0.1 MPa
		J·K-1 mol-1						kJ·mol-1
T/K		Cp°		S°		-[G°-H°(Tr)]/T		H-H°(Tr)		fH°		fG°		log Kf
0		0.		0.		INFINITE		-5.007		0.		0.		0.
100		16.010		10.034		53.414		-4.338		0.		0.		0.
200		22.631		23.730		35.354		-2.325		0.		0.		0.
250		23.782		28.915		33.563		-1.162		0.		0.		0.
298.15		24.442		33.164		33.164		0.		0.		0.		0.
300		24.462		33.315		33.164		0.045		0.		0.		0.
350		24.975		37.127		33.464		1.282		0.		0.		0.
400		25.318		40.484		34.136		2.539		0.		0.		0.
450		25.686		43.489		35.011		3.815		0.		0.		0.
500		25.912		46.206		35.997		5.105		0.		0.		0.
600		26.481		50.982		38.107		7.725		0.		0.		0.
700		26.996		55.103		40.247		10.399		0.		0.		0.
800		27.494		58.739		42.336		13.123		0.		0.		0.
900		28.049		62.009		44.343		15.899		0.		0.		0.
1000		28.662		64.994		46.261		18.733		0.		0.		0.
1100		29.479		67.763		48.091		21.638		0.		0.		0.
1200		30.519		70.368		49.840		24.633		0.		0.		0.
1300		32.143		72.871		51.516		27.762		0.		0.		0.
1358.000		33.353		74.300		52.459		29.660		CRYSTAL <--> LIQUID
1358.000		32.844		83.974		52.459		42.798		TRANSITION
1400		32.844		84.974		53.419		44.177		0.		0.		0.
1500		32.844		87.240		55.599		47.462		0.		0.		0.
1600		32.844		89.360		57.644		50.746		0.		0.		0.
1700		32.844		91.351		59.569		54.031		0.		0.		0.
1800		32.844		93.229		61.387		57.315		0.		0.		0.
1900		32.844		95.004		63.110		60.600		0.		0.		0.
2000		32.844		96.689		64.747		63.884		0.		0.		0.
2100		32.844		98.292		66.307		67.168		0.		0.		0.
2200		32.844		99.819		67.795		70.453		0.		0.		0.
2300		32.844		101.279		69.220		73.737		0.		0.		0.
2400		32.844		102.677		70.585		77.022		0.		0.		0.
2500		32.844		104.018		71.896		80.306		0.		0.		0.
2600		32.844		105.306		73.156		83.591		0.		0.		0.
2700		32.844		106.546		74.370		86.875		0.		0.		0.
2800		32.844		107.740		75.540		90.159		0.		0.		0.
2843.261		32.844		108.244		76.034		91.580		FUGACITY = 1 bar
2900		32.844		108.893		76.671		93.444		300.204 5.996 0.108
3000		32.844		110.006		77.764		96.728		-299.409		16.541		-0.288
3100		32.844		111.083		78.821		100.013		-298.665		27.060		-0.456
3200		32.844		112.126		79.846		103.297		-297.971		37.556		-0.613
3300		32.844		113.137		80.839		106.582		-297.328		48.031		-0.760
3400		32.844		114.117		81.804		109.866		-296.737		58.488		-0.899
3500		32.844		115.069		82.741		113.151		-296.195		68.927		-1.029
3600		32.844		115.995		83.652		116.435		-295.703		79.352		-1.151
3700		32.844		116.894		84.538		119.719		-295.259		89.764		-1.267
3800		32.844		117.770		85.401		123.004		-294.862		100.165		-1.377
3900		32.844		118.624		86.242		126.288		-294.509		110.556		-1.481
4000		32.844		119.455		87.062		129.573		-294.199		120.938		-1.579
PREVIOUS:								CURRENT: June 1977
Copper (Cu)								Cu1(cr,l)

Download table in tab-delimited text format.