Zirconium Fluoride (ZrF2)								F2Zr1(cr,l)
Enthalpy Reference Temperature = Tr = 298.15 K								Standard State Pressure = p° = 0.1 MPa
		J·K-1 mol-1						kJ·mol-1
T/K		Cp°		S°		-[G°-H°(Tr)]/T		H-H°(Tr)		fH°		fG°		log Kf
0
100
200
298.15		65.940		75.312		75.312		0.		-962.320		-912.724		159.905
300		66.024		75.720		75.313		0.122		-962.303		-912.416		158.866
400		69.873		95.253		77.950		6.921		-961.282		-895.937		116.997
500		73.220		111.212		83.054		14.079		-960.115		-879.733		91.905
600		76.149		124.827		88.908		21.551		-958.807		-863.777		75.198
700		78.659		136.761		94.909		29.296		-957.380		-848.050		63.282
800		80.626		147.395		100.817		37.262		-955.874		-832.533		54.359
900		82.425		156.997		106.535		45.416		-954.322		-817.209		47.430
1000		84.015		165.766		112.026		53.741		-952.743		-802.058		41.895
1100		85.270		173.834		117.283		62.206		-951.168		-787.066		37.375
1175.000		86.107		179.486		121.074		68.633		CRYSTAL <--> LIQUID
1175.000		100.416		211.534		121.074		106.289		TRANSITION
1200		100.416		213.648		122.981		108.800		-915.322		-772.800		33.639
1300		100.416		221.685		130.269		118.841		-911.919		-761.061		30.580
1400		100.416		229.127		137.068		128.883		-908.578		-749.583		27.967
1500		100.416		236.055		143.438		138.925		-905.311		-738.340		25.711
1600		100.416		242.536		149.432		148.966		-902.125		-727.313		23.744
1700		100.416		248.623		155.089		159.008		-899.029		-716.483		22.015
1800		100.416		254.363		160.447		169.049		-896.033		-705.832		20.483
1900		100.416		259.792		165.534		179.091		-893.144		-695.344		19.116
2000		100.416		264.943		170.376		189.133		-890.371		-685.006		17.891
2100		100.416		269.842		174.997		199.174		-887.719		-674.803		16.785
2200		100.416		274.513		179.415		209.216		-906.521		-663.979		15.765
2300		100.416		278.977		183.648		219.257		-904.551		-652.998		14.830
2400		100.416		283.251		187.709		229.299		-902.577		-642.103		13.975
2500		100.416		287.350		191.614		239.341		-900.594		-631.291		13.190
2600		100.416		291.288		195.372		249.382		-898.599		-620.558		12.467
2700		100.416		295.078		198.995		259.424		-896.587		-609.902		11.799
2800		100.416		298.730		202.492		269.465		-894.557		-599.321		11.180
2900		100.416		302.254		205.872		279.507		-892.505		-588.813		10.606
3000		100.416		305.658		209.142		289.549		-890.429		-578.377		10.070
PREVIOUS:								CURRENT: June 1969
Zirconium Fluoride (ZrF2)								F2Zr1(cr,l)

Download table in tab-delimited text format.