Iron (Fe)								Fe1(l)
Enthalpy Reference Temperature = Tr = 298.15 K								Standard State Pressure = p° = 0.1 MPa
		J·K-1 mol-1						kJ·mol-1
T/K		Cp°		S°		-[G°-H°(Tr)]/T		H-H°(Tr)		fH°		fG°		log Kf
0
100
200
250
298.15		25.096		34.763		34.763		0.		12.395		10.177		-1.783
300		25.142		34.918		34.764		0.046		12.395		10.163		-1.769
350		26.254		38.877		35.074		1.331		12.394		9.791		-1.461
400		27.384		42.457		35.776		2.672		12.393		9.419		-1.230
450		28.542		45.749		36.704		4.070		12.394		9.047		-1.050
500		29.702		48.816		37.763		5.526		12.395		8.675		-0.906
600		32.033		54.437		40.082		8.613		12.396		7.931		-0.690
700		34.363		59.550		42.503		11.933		12.389		7.187		-0.536
800		36.694		64.291		44.934		15.486		12.328		6.447		-0.421
900		39.024		68.747		47.334		19.272		12.085		5.724		-0.332
1000		41.355		72.980		49.689		23.291		11.356		5.049		-0.264
1100		43.689		77.031		51.992		27.543		9.966		4.501		-0.214
1200		46.024		80.932		54.242		32.028		9.362		4.014		-0.175
1200.000		46.024		80.932		54.242		32.028		GLASS <--> LIQUID
1200.000		46.024		80.932		54.242		32.028		TRANSITION
1300		46.024		84.616		56.438		36.631		10.521		3.521		-0.141
1400		46.024		88.027		58.574		41.233		11.596		2.941		-0.110
1500		46.024		91.202		60.645		45.836		12.588		2.288		-0.080
1600		46.024		94.172		62.649		50.438		13.495		1.571		-0.051
1700		46.024		96.963		64.586		55.040		13.370		0.819		-0.025
1800		46.024		99.593		66.458		59.643		13.776		0.069		-0.002
1809.000		46.024		99.823		66.624		60.057		DELTA <--> LIQUID
1900		46.024		102.082		68.268		64.245		0. 0. 0.
2000		46.024		104.442		70.019		68.848		0.		0.		0.
2100		46.024		106.688		71.712		73.450		0.		0.		0.
2200		46.024		108.829		73.351		78.052		0.		0.		0.
2300		46.024		110.875		74.938		82.655		0.		0.		0.
2400		46.024		112.834		76.476		87.257		0.		0.		0.
2500		46.024		114.712		77.968		91.860		0.		0.		0.
2600		46.024		116.517		79.417		96.462		0.		0.		0.
2700		46.024		118.254		80.823		101.064		0.		0.		0.
2800		46.024		119.928		82.190		105.667		0.		0.		0.
2900		46.024		121.543		83.519		110.269		0.		0.		0.
3000		46.024		123.103		84.813		114.872		0.		0.		0.
3100		46.024		124.613		86.073		119.474		0.		0.		0.
3133.345		46.024		125.105		86.485		121.009		FUGACITY = 1 bar
3200		46.024		126.074		87.300		124.076		348.300 7.424 0.121
3300		46.024		127.490		88.496		128.679		-346.399		18.511		-0.293
3400		46.024		128.864		89.664		133.281		-344.531		29.541		-0.454
3500		46.024		130.198		90.803		137.884		-342.697		40.516		-0.605
3600		46.024		131.495		91.915		142.486		-340.896		51.439		-0.746
3700		46.024		132.756		93.002		147.088		-339.131		62.313		-0.880
3800		46.024		133.983		94.064		151.691		-337.401		73.140		-1.005
3900		46.024		135.179		95.103		156.293		-335.707		83.921		-1.124
4000		46.024		136.344		96.120		160.896		-334.051		94.660		-1.236
PREVIOUS: March 1965								CURRENT: March 1978
Iron (Fe)								Fe1(l)

Download table in tab-delimited text format.