Iron (Fe)								Fe1(cr,l)
Enthalpy Reference Temperature = Tr = 298.15 K								Standard State Pressure = p° = 0.1 MPa
		J·K-1 mol-1						kJ·mol-1
T/K		Cp°		S°		-[G°-H°(Tr)]/T		H-H°(Tr)		fH°		fG°		log Kf
0		0.		0.		INFINITE		-4.507		0.		0.		0.
100		12.101		6.065		46.905		-4.084		0.		0.		0.
200		21.588		17.949		29.524		-2.315		0.		0.		0.
298.15		25.094		27.321		27.321		0.		0.		0.		0.
300		25.140		27.476		27.321		0.046		0.		0.		0.
400		27.386		35.021		28.335		2.674		0.		0.		0.
500		29.702		41.377		30.323		5.527		0.		0.		0.
600		32.049		46.997		32.642		8.613		0.		0.		0.
700		34.602		52.119		35.063		11.939		0.		0.		0.
800		37.949		56.940		37.498		15.553		0.		0.		0.
900		43.095		61.679		39.922		19.582		0.		0.		0.
1000		54.434		66.672		42.342		24.329		0.		0.		0.
1042.000		83.680		69.245		43.372		26.960		Cp LAMBDA MAXIMUM
1042.000		83.681		69.245		43.372		26.960		TRANSITION
1100		46.401		72.062		44.815		29.972		0.		0.		0.
1184.000		41.422		75.260		46.865		33.619		ALPHA <--> GAMMA
1184.000		33.882		76.020		46.865		34.519		TRANSITION
1200		34.016		76.476		47.257		35.062		0.		0.		0.
1300		34.853		79.231		49.612		38.505		0.		0.		0.
1400		35.690		81.845		51.822		42.033		0.		0.		0.
1500		36.526		84.336		53.907		45.643		0.		0.		0.
1600		37.363		86.720		55.884		49.338		0.		0.		0.
1665.000		37.907		88.218		57.117		51.784		GAMMA <--> DELTA
1665.000		41.112		88.721		57.117		52.621		TRANSITION
1700		41.463		89.580		57.776		54.066		0.		0.		0.
1800		42.468		91.978		59.610		58.263		0.		0.		0.
1809.000		42.558		92.190		59.772		58.645		DELTA <--> LIQUID
1809.000		46.024		99.823		59.772		72.452		TRANSITION
1900		46.024		102.082		61.744		76.641		0.		0.		0.
2000		46.024		104.442		63.821		81.243		0.		0.		0.
2100		46.024		106.688		65.809		85.845		0.		0.		0.
2200		46.024		108.829		67.716		90.448		0.		0.		0.
2300		46.024		110.875		69.549		95.050		0.		0.		0.
2400		46.024		112.833		71.312		99.653		0.		0.		0.
2500		46.024		114.712		73.010		104.255		0.		0.		0.
2600		46.024		116.517		74.649		108.857		0.		0.		0.
2700		46.024		118.254		76.232		113.460		0.		0.		0.
2800		46.024		119.928		77.763		118.062		0.		0.		0.
2900		46.024		121.543		79.245		122.665		0.		0.		0.
3000		46.024		123.103		80.681		127.267		0.		0.		0.
3100		46.024		124.613		82.074		131.869		0.		0.		0.
3133.345		46.024		125.105		82.529		133.404		FUGACITY = 1 bar
3200		46.024		126.074		83.426		136.472		348.300 7.424 0.121
3300		46.024		127.490		84.740		141.074		-346.399		18.511		-0.293
3400		46.024		128.864		86.018		145.677		-344.531		29.541		-0.454
3500		46.024		130.198		87.261		150.279		-342.697		40.516		-0.605
3600		46.024		131.495		88.472		154.881		-340.896		51.439		-0.746
3700		46.024		132.756		89.652		159.484		-339.131		62.313		-0.880
3800		46.024		133.983		90.802		164.086		-337.401		73.140		-1.005
3900		46.024		135.179		91.925		168.689		-335.707		83.921		-1.124
4000		46.024		136.344		93.021		173.291		-334.051		94.660		-1.236
PREVIOUS:								CURRENT: March 1978
Iron (Fe)								Fe1(cr,l)

Download table in tab-delimited text format.