		J·K^-1 mol^-1						kJ·mol^-1
Gallium (Ga)								Ga₁(cr,l)

Enthalpy Reference Temperature = T_r = 298.15 K								Standard State Pressure = p° = 0.1 MPa
T/K		C_p^°		S^°		-[G^°-H^°(T_r)]/T		H-H^°(T_r)		_fH^°		_fG^°		log K_f
0		0.		0.		INFINITE		-5.561		0.		0.		0.
100		18.484		16.085		62.261		-4.618		0.		0.		0.
200		23.815		30.912		43.151		-2.448		0.		0.		0.
250		24.907		36.338		41.262		-1.231		0.		0.		0.

298.15		26.064		40.838		40.838		0.		0.		0.		0.

300		26.091		41.000		40.839		0.048		0.		0.		0.

302.920		26.133		41.253		40.842		0.124		CRYSTAL <--> LIQUID
302.920		28.493		59.706		40.842		5.714		TRANSITION

350		27.719		63.764		43.660		7.037		0.		0.		0.
400		27.154		67.426		46.408		8.407		0.		0.		0.
450		26.961		70.613		48.924		9.760		0.		0.		0.
500		26.819		73.445		51.237		11.104		0.		0.		0.

600		26.694		78.324		55.358		13.780		0.		0.		0.
700		26.568		82.428		58.939		16.442		0.		0.		0.
800		26.568		85.976		62.102		19.099		0.		0.		0.
900		26.568		89.105		64.932		21.756		0.		0.		0.
1000		26.568		91.904		67.492		24.413		0.		0.		0.

1100		26.568		94.436		69.828		27.069		0.		0.		0.
1200		26.568		96.748		71.976		29.726		0.		0.		0.
1300		26.568		98.875		73.965		32.383		0.		0.		0.
1400		26.568		100.844		75.815		35.040		0.		0.		0.
1500		26.568		102.677		77.546		37.697		0.		0.		0.

1600		26.568		104.391		79.171		40.354		0.		0.		0.
1700		26.568		106.002		80.702		43.010		0.		0.		0.
1800		26.568		107.521		82.150		45.667		0.		0.		0.
1900		26.568		108.957		83.524		48.324		0.		0.		0.
2000		26.568		110.320		84.830		50.981		0.		0.		0.

2100		26.568		111.616		86.075		53.638		0.		0.		0.
2200		26.568		112.852		87.264		56.295		0.		0.		0.
2300		26.568		114.033		88.402		58.951		0.		0.		0.
2400		26.568		115.164		89.494		61.608		0.		0.		0.

2476.570		26.568		115.998		90.301		63.643		FUGACITY = 1 bar

2500		26.568		116.249		90.543		64.265		258.586 2.447 0.051

2600		26.568		117.291		91.551		66.922		-258.052		12.878		-0.259
2700		26.568		118.293		92.523		69.579		-257.515		23.288		-0.451
2800		26.568		119.260		93.461		72.236		-256.975		33.679		-0.628
2900		26.568		120.192		94.367		74.892		-256.433		44.050		-0.793
3000		26.568		121.093		95.243		77.549		-255.888		54.402		-0.947

PREVIOUS:								CURRENT: June 1970

Gallium (Ga)								Ga₁(cr,l)

Download table in tab-delimited text format.