		J·K^-1 mol^-1						kJ·mol^-1
Lithium Silicate (Li₂SiO₃)								Li₂O₃Si₁(l)

Enthalpy Reference Temperature = T_r = 298.15 K								Standard State Pressure = p° = 0.1 MPa
T/K		C_p^°		S^°		-[G^°-H^°(T_r)]/T		H-H^°(T_r)		_fH^°		_fG^°		log K_f
0
100
200

298.15		100.567		96.064		96.064		0.		-1625.231		-1539.171		269.656

300		101.010		96.688		96.066		0.186		-1625.254		-1538.637		267.901
400		118.826		128.398		100.268		11.252		-1625.968		-1509.633		197.138
500		127.809		155.924		108.716		23.604		-1632.348		-1479.892		154.603

600		134.306		179.818		118.619		36.720		-1632.314		-1449.396		126.181
700		139.649		200.930		128.898		50.422		-1631.792		-1418.944		105.883
800		144.432		219.897		139.108		64.632		-1630.889		-1388.595		90.666
900		148.565		237.151		149.057		79.285		-1629.689		-1358.378		78.838
1000		152.302		253.001		158.670		94.331		-1628.218		-1328.309		69.384


1000.000		152.302		253.001		158.670		94.331		GLASS <--> LIQUID
1000.000		167.360		253.001		158.670		94.331		TRANSITION

1100		167.360		268.952		167.982		111.067		-1625.164		-1298.466		61.659
1200		167.360		283.514		177.012		127.803		-1622.201		-1268.898		55.234
1300		167.360		296.910		185.726		144.539		-1619.325		-1239.573		49.807
1400		167.360		309.313		194.116		161.275		-1616.524		-1210.467		45.163

1474.000		167.360		317.933		200.118		173.660		CRYSTAL <--> LIQUID

1500		167.360		320.860		202.185		178.011		1613.789 1181.559 41.146

1600		167.360		331.661		209.944		194.747		-1611.119		-1152.831		37.636
1700		167.360		341.807		217.405		211.483		-1949.160		-1109.469		34.090
1800		167.360		351.373		224.584		228.219		-1944.879		-1060.199		30.766
1900		167.360		360.422		231.498		244.955		-1940.635		-1011.166		27.799
2000		167.360		369.006		238.160		261.691		-1936.429		-962.356		25.134

2100		167.360		377.172		244.587		278.427		-1932.264		-913.755		22.728
2200		167.360		384.957		250.792		295.163		-1928.141		-865.350		20.546
2300		167.360		392.397		256.788		311.899		-1924.060		-817.134		18.558
2400		167.360		399.519		262.588		328.635		-1920.026		-769.094		16.739
2500		167.360		406.351		268.203		345.371		-1916.040		-721.220		15.069

2600		167.360		412.915		273.643		362.107		-1912.104		-673.505		13.531
2700		167.360		419.232		278.919		378.843		-1908.221		-625.940		12.110
2800		167.360		425.318		284.040		395.579		-1904.393		-578.518		10.792
2900		167.360		431.191		289.013		412.315		-1900.623		-531.233		9.569
3000		167.360		436.865		293.848		429.051		-1896.915		-484.076		8.429

3100		167.360		442.352		298.550		445.787		-1893.268		-437.041		7.364
3200		167.360		447.666		303.127		462.523		-1889.688		-390.124		6.368
3300		167.360		452.816		307.586		479.259		-1886.174		-343.318		5.434
3400		167.360		457.812		311.931		495.995		-1882.730		-296.616		4.557
3500		167.360		462.663		316.169		512.731		-1879.358		-250.015		3.731

3600		167.360		467.378		320.304		529.467		-2260.212		-193.048		2.801
3700		167.360		471.964		324.341		546.203		-2256.576		-135.678		1.915
3800		167.360		476.427		328.285		562.939		-2253.020		-78.403		1.078
3900		167.360		480.774		332.139		579.675		-2249.546		-21.221		0.284
4000		167.360		485.011		335.908		596.411		-2246.155		35.871		-0.468

PREVIOUS: March 1964								CURRENT: June 1967

Lithium Silicate (Li₂SiO₃)								Li₂O₃Si₁(l)

Download table in tab-delimited text format.