		J·K^-1 mol^-1						kJ·mol^-1
Lithium Silicate (Li₂SiO₃)								Li₂O₃Si₁(cr,l)

Enthalpy Reference Temperature = T_r = 298.15 K								Standard State Pressure = p° = 0.1 MPa
T/K		C_p^°		S^°		-[G^°-H^°(T_r)]/T		H-H^°(T_r)		_fH^°		_fG^°		log K_f
0		0.		0.		INFINITE		-14.554		-1638.567		-1638.567		INFINITE
100		27.669		12.276		148.950		-13.667		-1643.293		-1616.673		844.463
200		72.036		45.798		88.665		-8.573		-1647.428		-1588.278		414.816

298.15		100.567		80.295		80.295		0.		-1649.500		-1558.739		273.085

300		101.010		80.919		80.297		0.186		-1649.524		-1558.176		271.303
400		118.826		112.628		84.499		11.252		-1650.237		-1527.594		199.483
500		127.809		140.155		92.946		23.604		-1656.617		-1496.277		156.315

600		134.306		164.049		102.850		36.720		-1656.584		-1464.203		127.470
700		139.649		185.161		113.129		50.422		-1656.061		-1432.175		106.870
800		144.432		204.128		123.338		64.632		-1655.158		-1400.249		91.427
900		148.565		221.382		133.288		79.285		-1653.958		-1368.455		79.423
1000		152.302		237.232		142.900		94.331		-1652.487		-1336.808		69.828

1100		155.576		251.903		152.151		109.728		-1650.773		-1305.321		61.985
1200		158.574		265.571		161.040		125.437		-1648.837		-1274.001		55.456
1300		161.293		278.371		169.578		141.431		-1646.703		-1242.850		49.938
1400		163.942		290.422		177.783		157.694		-1644.375		-1211.870		45.215

1474.000		165.856		298.915		183.653		169.896		CRYSTAL <--> LIQUID
1474.000		167.360		317.933		183.653		197.929		TRANSITION

1500		167.360		320.860		186.006		202.281		-1613.789		-1181.559		41.146

1600		167.360		331.661		194.775		219.017		-1611.119		-1152.831		37.636
1700		167.360		341.807		203.129		235.753		-1949.160		-1109.469		34.090
1800		167.360		351.373		211.102		252.489		-1944.879		-1060.199		30.766
1900		167.360		360.422		218.725		269.225		-1940.635		-1011.166		27.799
2000		167.360		369.006		226.026		285.961		-1936.429		-962.356		25.134

2100		167.360		377.172		233.030		302.697		-1932.264		-913.755		22.728
2200		167.360		384.957		239.761		319.433		-1928.141		-865.350		20.546
2300		167.360		392.397		246.236		336.169		-1924.060		-817.134		18.558
2400		167.360		399.519		252.476		352.905		-1920.026		-769.094		16.739
2500		167.360		406.351		258.495		369.641		-1916.040		-721.220		15.069

2600		167.360		412.915		264.309		386.377		-1912.104		-673.505		13.531
2700		167.360		419.232		269.931		403.113		-1908.221		-625.940		12.110
2800		167.360		425.318		275.372		419.849		-1904.393		-578.518		10.792
2900		167.360		431.191		280.645		436.585		-1900.623		-531.233		9.569
3000		167.360		436.865		285.758		453.321		-1896.915		-484.076		8.429

3100		167.360		442.352		290.721		470.057		-1893.268		-437.041		7.364
3200		167.360		447.666		295.543		486.793		-1889.688		-390.124		6.368
3300		167.360		452.816		300.231		503.529		-1886.174		-343.318		5.434
3400		167.360		457.812		304.793		520.265		-1882.730		-296.616		4.557
3500		167.360		462.663		309.235		537.001		-1879.358		-250.015		3.731

3600		167.360		467.378		313.562		553.737		-2260.212		-193.048		2.801
3700		167.360		471.964		317.782		570.473		-2256.576		-135.678		1.915
3800		167.360		476.427		321.898		587.209		-2253.020		-78.403		1.078
3900		167.360		480.774		325.916		603.945		-2249.546		-21.221		0.284
4000		167.360		485.011		329.841		620.681		-2246.155		35.871		-0.468