Lithium Titanium Oxide (Li2TiO3) Li2O3Ti1(cr)
 
Enthalpy Reference Temperature = Tr = 298.15 K Standard State Pressure = p° = 0.1 MPa
  J·K-1 mol-1 kJ·mol-1  
T/K Cp° S° -[G°-H°(Tr)]/T H-H°(Tr) fH° fG° log Kf
0 0. 0. INFINITE -16.493 -1660.065 -1660.065 INFINITE
100 31.142 14.129 169.105 -15.498 -1664.977 -1638.099 855.655
200 82.663 52.886 101.316 -9.686 -1669.132 -1609.488 420.355
 
298.15 109.855 91.755 91.755 0. -1670.671 -1579.767 276.769
 
300 110.750 92.437 91.757 0.204 -1670.687 -1579.203 274.964
400 127.361 126.619 96.309 12.124 -1671.038 -1548.635 202.231
500 135.645 156.002 105.388 25.307 -1677.049 -1517.421 158.524
 
600 141.503 181.283 115.979 39.182 -1676.706 -1485.520 129.326
700 145.854 203.436 126.924 53.559 -1675.949 -1453.710 108.477
800 149.034 223.130 137.741 68.311 -1674.920 -1422.030 92.849
900 151.670 240.839 148.229 83.349 -1673.763 -1390.488 80.702
1000 153.888 256.936 158.307 98.628 -1672.570 -1359.077 70.991
 
1100 155.812 271.696 167.954 114.117 -1671.422 -1327.783 63.051
1200 157.318 285.322 177.174 129.778 -1674.331 -1296.471 56.434
1300 158.490 297.965 185.985 145.574 -1672.635 -1265.052 50.830
1400 159.494 309.751 194.410 161.478 -1670.942 -1233.763 46.032
 
1485.000 160.344 319.174 201.284 175.067 ALPHA <--> BETA
1485.000 176.063 326.922 201.284 186.573 TRANSITION
 
1500 176.565 328.694 202.549 189.218 -1657.529 -1202.712 41.882
 
1600 179.912 340.196 210.795 207.042 -1654.160 -1172.500 38.278
1700 183.259 351.204 218.733 225.200 -1941.066 -1128.152 34.664
1800 186.606 361.773 226.388 243.693 -1935.811 -1080.485 31.355
 
1820.000 187.276 363.839 227.887 247.432 BETA <--> LIQUID
 
1900 189.954 371.952 233.783 262.521 1930.404 1033.113 28.402
2000 193.301 381.781 240.939 281.684 -1939.544 -985.576 25.741
 
2100 196.648 391.293 247.873 301.182 -1934.622 -937.998 23.331
2200 199.995 400.518 254.603 321.014 -1929.406 -890.660 21.147
2300 203.342 409.482 261.143 341.181 -1923.899 -843.567 19.158
2400 206.690 418.207 267.506 361.682 -1918.103 -796.720 17.340
2500 210.037 426.712 273.705 382.519 -1912.021 -750.119 15.673
 
2600 213.384 435.015 279.750 403.690 -1905.654 -703.768 14.139
2700 216.731 443.131 285.652 425.195 -1899.005 -657.666 12.723
2800 220.078 451.074 291.418 447.036 -1892.077 -611.816 11.414
2900 223.426 458.855 297.058 469.211 -1884.873 -566.220 10.199
3000 226.773 466.486 302.579 491.721 -1877.394 -520.876 9.069
 
PREVIOUS: June 1961 CURRENT: March 1964
 
Lithium Titanium Oxide (Li2TiO3) Li2O3Ti1(cr)

Download table in tab-delimited text format.