Lithium Titanium Oxide (Li2TiO3) Li2O3Ti1(l)
 
Enthalpy Reference Temperature = Tr = 298.15 K Standard State Pressure = p° = 0.1 MPa
  J·K-1 mol-1 kJ·mol-1  
T/K Cp° S° -[G°-H°(Tr)]/T H-H°(Tr) fH° fG° log Kf
0              
100              
200              
 
298.15 109.855 147.656 147.656 0. -1566.760 -1492.523 261.484
 
300 110.750 148.338 147.658 0.204 -1566.775 -1492.062 259.791
400 127.361 182.520 152.209 12.124 -1567.127 -1467.084 191.582
500 135.645 211.903 161.289 25.307 -1573.138 -1441.460 150.588
 
600 141.503 237.183 171.880 39.182 -1572.795 -1415.149 123.200
700 145.854 259.337 182.824 53.559 -1572.038 -1388.930 103.643
800 149.034 279.031 193.642 68.311 -1571.009 -1362.840 88.984
900 151.670 296.740 204.130 83.349 -1569.852 -1336.887 77.591
1000 153.888 312.837 214.208 98.628 -1568.659 -1311.066 68.483
 
1100 155.812 327.597 223.855 114.117 -1567.511 -1285.363 61.037
1200 157.318 341.223 233.075 129.778 -1570.420 -1259.641 54.831
 
1214.000 157.569 343.049 234.333 131.982 GLASS <--> LIQUID
1214.000 200.832 343.049 234.333 131.982 TRANSITION
 
1300 200.832 356.795 241.984 149.253 -1565.044 -1233.940 49.580
1400 200.832 371.678 250.723 169.336 -1559.172 -1208.691 45.097
1500 200.832 385.534 259.254 189.420 -1553.416 -1183.859 41.226
 
1600 200.832 398.495 267.556 209.503 -1547.787 -1159.406 37.851
1700 200.832 410.671 275.620 229.586 -1832.769 -1120.948 34.443
1800 200.832 422.150 283.445 249.669 -1825.924 -1079.275 31.320
 
1820.000 200.832 424.369 284.965 253.716 BETA <--> LIQUID
 
1900 200.832 433.008 291.033 269.752 1819.262 1037.977 28.536
2000 200.832 443.310 298.392 289.836 -1827.482 -996.572 26.028
 
2100 200.832 453.108 305.528 309.919 -1821.974 -955.162 23.758
2200 200.832 462.451 312.450 330.002 -1816.507 -914.012 21.701
2300 200.832 471.378 319.167 350.085 -1811.084 -873.112 19.829
2400 200.832 479.926 325.689 370.168 -1805.706 -832.447 18.118
2500 200.832 488.124 332.023 390.252 -1800.377 -792.004 16.548
 
2600 200.832 496.001 338.180 410.335 -1795.098 -751.773 15.103
2700 200.832 503.580 344.166 430.418 -1789.872 -711.744 13.770
2800 200.832 510.884 349.991 450.501 -1784.701 -671.908 12.535
2900 200.832 517.931 355.661 470.584 -1779.588 -632.257 11.388
3000 200.832 524.740 361.184 490.668 -1774.536 -592.780 10.321
 
3100 200.832 531.325 366.567 510.751 -1769.547 -553.470 9.326
3200 200.832 537.701 371.816 530.834 -1764.623 -514.321 8.395
3300 200.832 543.881 376.937 550.917 -1759.766 -475.325 7.524
3400 200.832 549.877 381.935 571.000 -1754.979 -436.474 6.706
3500 200.832 555.698 386.817 591.084 -1750.265 -397.763 5.936
 
3600 200.832 561.356 391.587 611.167 -1745.624 -359.186 5.212
3700 200.832 566.859 396.250 631.250 -2150.157 -312.949 4.418
3800 200.832 572.214 400.811 651.333 -2144.436 -263.371 3.620
3900 200.832 577.431 405.273 671.416 -2138.850 -213.942 2.865
4000 200.832 582.516 409.641 691.500 -2133.402 -164.655 2.150
 
PREVIOUS: June 1961 CURRENT: March 1964
 
Lithium Titanium Oxide (Li2TiO3) Li2O3Ti1(l)

Download table in tab-delimited text format.