Lithium Titanium Oxide (Li2TiO3) Li2O3Ti1(cr,l)
 
Enthalpy Reference Temperature = Tr = 298.15 K Standard State Pressure = p° = 0.1 MPa
  J·K-1 mol-1 kJ·mol-1  
T/K Cp° S° -[G°-H°(Tr)]/T H-H°(Tr) fH° fG° log Kf
0 0. 0. INFINITE -16.493 -1660.065 -1660.065 INFINITE
100 31.142 14.129 169.105 -15.498 -1664.977 -1638.099 855.655
200 82.663 52.886 101.316 -9.686 -1669.132 -1609.488 420.355
 
298.15 109.855 91.755 91.755 0. -1670.671 -1579.767 276.769
 
300 110.750 92.437 91.757 0.204 -1670.687 -1579.203 274.964
400 127.361 126.619 96.309 12.124 -1671.038 -1548.635 202.231
500 135.645 156.002 105.388 25.307 -1677.049 -1517.421 158.524
 
600 141.503 181.283 115.979 39.182 -1676.706 -1485.520 129.326
700 145.854 203.436 126.924 53.559 -1675.949 -1453.710 108.477
800 149.034 223.130 137.741 68.311 -1674.920 -1422.030 92.849
900 151.670 240.839 148.229 83.349 -1673.763 -1390.488 80.702
1000 153.888 256.936 158.307 98.628 -1672.570 -1359.077 70.991
 
1100 155.812 271.696 167.954 114.117 -1671.422 -1327.783 63.051
1200 157.318 285.322 177.174 129.778 -1674.331 -1296.471 56.434
1300 158.490 297.965 185.985 145.574 -1672.635 -1265.052 50.830
1400 159.494 309.751 194.410 161.478 -1670.942 -1233.763 46.032
 
1485.000 160.344 319.174 201.284 175.067 ALPHA <--> BETA
1485.000 176.063 326.922 201.284 186.573 TRANSITION
 
1500 176.565 328.694 202.549 189.218 -1657.529 -1202.712 41.882
 
1600 179.912 340.196 210.795 207.042 -1654.160 -1172.500 38.278
1700 183.259 351.204 218.733 225.200 -1941.066 -1128.152 34.664
1800 186.606 361.773 226.388 243.693 -1935.811 -1080.485 31.355
 
1820.000 187.276 363.839 227.887 247.432 BETA <--> LIQUID
1820.000 200.832 424.369 227.887 357.597 TRANSITION
 
1900 200.832 433.008 236.343 373.664 -1819.262 -1037.977 28.536
2000 200.832 443.310 246.436 393.747 -1827.482 -996.572 26.028
 
2100 200.832 453.108 256.046 413.830 -1821.974 -955.162 23.758
2200 200.832 462.451 265.218 433.913 -1816.507 -914.012 21.701
2300 200.832 471.378 273.989 453.996 -1811.084 -873.112 19.829
2400 200.832 479.926 282.392 474.080 -1805.706 -832.447 18.118
2500 200.832 488.124 290.459 494.163 -1800.377 -792.004 16.548
 
2600 200.832 496.001 298.214 514.246 -1795.098 -751.773 15.103
2700 200.832 503.580 305.681 534.329 -1789.872 -711.744 13.770
2800 200.832 510.884 312.880 554.412 -1784.701 -671.908 12.535
2900 200.832 517.931 319.830 574.496 -1779.588 -632.257 11.388
3000 200.832 524.740 326.547 594.579 -1774.536 -592.780 10.321
 
3100 200.832 531.325 333.047 614.662 -1769.547 -553.470 9.326
3200 200.832 537.701 339.344 634.745 -1764.623 -514.321 8.395
3300 200.832 543.881 345.449 654.828 -1759.766 -475.325 7.524
3400 200.832 549.877 351.373 674.912 -1754.979 -436.474 6.706
3500 200.832 555.698 357.128 694.995 -1750.265 -397.763 5.936
 
3600 200.832 561.356 362.723 715.078 -1745.624 -359.186 5.212
3700 200.832 566.859 368.166 735.161 -2150.157 -312.949 4.418
3800 200.832 572.214 373.466 755.244 -2144.436 -263.371 3.620
3900 200.832 577.431 378.629 775.328 -2138.850 -213.942 2.865
4000 200.832 582.516 383.663 795.411 -2133.402 -164.655 2.150
 
PREVIOUS: CURRENT: March 1964
 
Lithium Titanium Oxide (Li2TiO3) Li2O3Ti1(cr,l)

Download table in tab-delimited text format.