Magnesium (Mg) | Mg1(cr,l) | |||||||||||||
Enthalpy Reference Temperature = Tr = 298.15 K | Standard State Pressure = p° = 0.1 MPa | |||||||||||||
J·K-1 mol-1 | kJ·mol-1 | |||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
T/K | Cp° | S° | -[G°-H°(Tr)]/T | H-H°(Tr) | ![]() |
![]() |
log Kf | |||||||
0 | 0. | 0. | INFINITE | -4.998 | 0. | 0. | 0. | |||||||
100 | 15.762 | 9.505 | 53.066 | -4.356 | 0. | 0. | 0. | |||||||
200 | 22.724 | 23.143 | 34.888 | -2.349 | 0. | 0. | 0. | |||||||
250 | 24.018 | 28.364 | 33.076 | -1.178 | 0. | 0. | 0. | |||||||
298.15 | 24.869 | 32.671 | 32.671 | 0. | 0. | 0. | 0. | |||||||
300 | 24.897 | 32.825 | 32.671 | 0.046 | 0. | 0. | 0. | |||||||
350 | 25.568 | 36.715 | 32.977 | 1.308 | 0. | 0. | 0. | |||||||
400 | 26.144 | 40.167 | 33.664 | 2.601 | 0. | 0. | 0. | |||||||
450 | 26.668 | 43.277 | 34.562 | 3.922 | 0. | 0. | 0. | |||||||
500 | 27.171 | 46.113 | 35.578 | 5.268 | 0. | 0. | 0. | |||||||
600 | 28.184 | 51.156 | 37.764 | 8.035 | 0. | 0. | 0. | |||||||
700 | 29.279 | 55.581 | 39.999 | 10.907 | 0. | 0. | 0. | |||||||
800 | 30.507 | 59.569 | 42.200 | 13.895 | 0. | 0. | 0. | |||||||
900 | 31.895 | 63.241 | 44.336 | 17.014 | 0. | 0. | 0. | |||||||
923.000 | 32.238 | 64.050 | 44.818 | 17.751 | CRYSTAL <--> LIQUID | |||||||||
923.000 | 34.309 | 73.234 | 44.818 | 26.228 | TRANSITION | |||||||||
1000 | 34.309 | 75.983 | 47.113 | 28.870 | 0. | 0. | 0. | |||||||
1100 | 34.309 | 79.253 | 49.888 | 32.301 | 0. | 0. | 0. | |||||||
1200 | 34.309 | 82.238 | 52.462 | 35.732 | 0. | 0. | 0. | |||||||
1300 | 34.309 | 84.984 | 54.859 | 39.163 | 0. | 0. | 0. | |||||||
1366.104 | 34.309 | 86.686 | 56.358 | 41.431 | FUGACITY = 1 bar | |||||||||
1400 | 34.309 | 87.527 | 57.103 | 42.594 | 127.409 3.167 0.118 | |||||||||
1500 | 34.309 | 89.894 | 59.211 | 46.024 | -126.057 | 12.447 | -0.433 | |||||||
1600 | 34.309 | 92.108 | 61.199 | 49.455 | -124.705 | 21.636 | -0.706 | |||||||
1700 | 34.309 | 94.188 | 63.079 | 52.886 | -123.352 | 30.741 | -0.945 | |||||||
1800 | 34.309 | 96.149 | 64.862 | 56.317 | -122.000 | 39.766 | -1.154 | |||||||
1900 | 34.309 | 98.004 | 66.558 | 59.748 | -120.648 | 48.717 | -1.339 | |||||||
2000 | 34.309 | 99.764 | 68.175 | 63.179 | -119.296 | 57.596 | -1.504 | |||||||
PREVIOUS: | CURRENT: September 1983 | |||||||||||||
Magnesium (Mg) | Mg1(cr,l) |