Magnesium Titanium Oxide (MgTiO3) Mg1O3Ti1(l)
 
Enthalpy Reference Temperature = Tr = 298.15 K Standard State Pressure = p° = 0.1 MPa
  J·K-1 mol-1 kJ·mol-1  
T/K Cp° S° -[G°-H°(Tr)]/T H-H°(Tr) fH° fG° log Kf
0              
100              
200              
 
298.15 91.881 111.082 111.082 0. -1497.631 -1420.091 248.794
 
300 92.203 111.651 111.083 0.170 -1497.635 -1419.610 247.176
400 105.244 140.132 114.878 10.102 -1497.329 -1393.623 181.988
500 113.123 164.524 122.429 21.047 -1496.378 -1367.797 142.893
 
600 118.453 185.647 131.245 32.641 -1495.117 -1342.196 116.849
700 122.353 204.213 140.370 44.690 -1493.710 -1316.819 98.262
800 125.382 220.756 149.403 57.082 -1492.236 -1291.649 84.336
900 127.846 235.670 158.173 69.747 -1490.789 -1266.664 73.515
1000 129.938 249.251 166.612 82.639 -1498.067 -1241.121 64.829
 
1100 131.775 261.723 174.699 95.726 -1496.990 -1215.479 57.718
1200 133.432 273.261 182.438 108.987 -1499.977 -1189.811 51.791
1300 134.972 284.003 189.842 122.409 -1498.342 -1164.030 46.771
 
1300.000 134.972 284.003 189.842 122.409 GLASS <--> LIQUID
1300.000 163.176 284.003 189.842 122.409 TRANSITION
 
1400 163.176 296.095 197.005 138.726 -1621.344 -1135.313 42.359
1500 163.176 307.353 203.991 155.044 -1615.717 -1100.794 38.333
 
1600 163.176 317.884 210.784 171.361 -1610.233 -1066.645 34.822
1700 163.176 327.777 217.378 187.679 -1604.905 -1032.835 31.735
1800 163.176 337.104 223.772 203.997 -1599.743 -999.334 29.000
1900 163.176 345.926 229.971 220.314 -1594.761 -966.115 26.560
 
1953.000 163.176 350.416 233.179 228.963 CRYSTAL <--> LIQUID
 
2000 163.176 354.296 235.980 236.632 1604.658 932.699 24.360
 
2100 163.176 362.258 241.805 252.949 -1600.822 -899.195 22.366
2200 163.176 369.848 247.454 269.267 -1597.019 -865.873 20.558
2300 163.176 377.102 252.935 285.585 -1593.251 -832.724 18.912
2400 163.176 384.047 258.254 301.902 -1589.518 -799.738 17.406
2500 163.176 390.708 263.420 318.220 -1585.818 -766.907 16.024
 
2600 163.176 397.108 268.439 334.537 -1582.152 -734.223 14.751
2700 163.176 403.266 273.320 350.855 -1578.520 -701.679 13.575
2800 163.176 409.200 278.067 367.173 -1574.922 -669.269 12.485
2900 163.176 414.926 282.688 383.490 -1571.357 -636.988 11.473
3000 163.176 420.458 287.189 399.808 -1567.828 -604.829 10.531
 
3100 163.176 425.809 291.575 416.125 -1564.332 -572.786 9.651
3200 163.176 430.989 295.851 432.443 -1560.871 -540.857 8.829
3300 163.176 436.011 300.023 448.761 -1557.446 -509.035 8.057
3400 163.176 440.882 304.094 465.078 -1554.057 -477.315 7.333
3500 163.176 445.612 308.070 481.396 -1550.706 -445.695 6.652
 
3600 163.176 450.209 311.955 497.713 -1547.392 -414.170 6.009
3700 163.176 454.680 315.752 514.031 -1953.217 -374.949 5.293
3800 163.176 459.031 319.466 530.349 -1948.749 -332.352 4.568
3900 163.176 463.270 323.099 546.666 -1944.379 -289.872 3.882
4000 163.176 467.401 326.655 562.984 -1940.107 -247.504 3.232
 
PREVIOUS: CURRENT: June 1967
 