Magnesium Titanium Oxide (Mg2TiO4) Mg2O4Ti1(cr)
 
Enthalpy Reference Temperature = Tr = 298.15 K Standard State Pressure = p° = 0.1 MPa
  J·K-1 mol-1 kJ·mol-1  
T/K Cp° S° -[G°-H°(Tr)]/T H-H°(Tr) fH° fG° log Kf
0 0. 0. INFINITE -18.836 -2151.027 -2151.027 INFINITE
100 34.639 26.740 204.267 -17.753 -2157.597 -2122.882 1108.880
200 94.320 70.337 125.901 -11.113 -2162.710 -2085.881 544.776
 
298.15 128.574 115.102 115.102 0. -2164.383 -2047.719 358.752
 
300 129.026 115.899 115.104 0.238 -2164.393 -2046.995 356.414
400 146.285 155.637 120.405 14.093 -2164.204 -2007.859 262.199
500 156.410 189.441 130.920 29.260 -2163.228 -1968.875 205.687
 
600 163.686 218.628 143.161 45.280 -2161.887 -1930.126 168.032
700 169.582 244.316 155.813 61.952 -2160.357 -1891.618 141.154
800 174.707 267.301 168.337 79.171 -2158.713 -1853.339 121.011
900 179.360 288.151 180.509 96.877 -2157.045 -1815.267 105.355
1000 183.686 307.275 192.243 115.032 -2172.648 -1775.953 92.766
 
1100 187.778 324.975 203.515 133.607 -2171.269 -1736.349 82.452
1200 191.690 341.483 214.332 152.581 -2173.748 -1696.756 73.858
1300 195.456 356.976 224.714 171.940 -2171.398 -1657.101 66.583
1400 199.091 371.594 234.689 191.668 -2423.636 -1611.300 60.118
1500 202.614 385.451 244.282 211.754 -2418.140 -1553.467 54.097
 
1600 206.041 398.637 253.520 232.188 -2412.452 -1496.007 48.840
1700 209.367 411.229 262.429 252.959 -2406.595 -1438.908 44.212
1800 212.610 423.288 271.033 274.058 -2400.588 -1382.158 40.109
1900 215.765 434.868 279.353 295.478 -2394.453 -1325.745 36.447
2000 218.840 446.014 287.410 317.209 -2402.896 -1269.205 33.148
 
 
2013.000 219.233 447.433 288.438 320.056 CRYSTAL <--> LIQUID
 
2100 221.831 456.764 295.220 339.243 2397.315 1212.657 30.163
2200 224.752 467.151 302.800 361.573 -2391.484 -1156.379 27.456
2300 227.593 477.205 310.165 384.191 -2385.411 -1100.373 24.990
2400 230.358 486.950 317.329 407.089 -2379.103 -1044.637 22.736
2500 233.049 496.408 324.304 430.260 -2372.570 -989.168 20.668
 
2600 235.668 505.600 331.101 453.696 -2365.816 -933.964 18.764
2700 238.212 514.542 337.730 477.391 -2358.852 -879.024 17.006
2800 240.685 523.250 344.201 501.336 -2351.684 -824.346 15.378
2900 243.086 531.738 350.522 525.525 -2344.320 -769.929 13.868
3000 245.417 540.018 356.701 549.951 -2336.769 -715.767 12.463
 
PREVIOUS: June 1961 CURRENT: June 1967
 
Magnesium Titanium Oxide (Mg2TiO4) Mg2O4Ti1(cr)

Download table in tab-delimited text format.