Magnesium Titanium Oxide (Mg2TiO4) Mg2O4Ti1(l)
 
Enthalpy Reference Temperature = Tr = 298.15 K Standard State Pressure = p° = 0.1 MPa
  J·K-1 mol-1 kJ·mol-1  
T/K Cp° S° -[G°-H°(Tr)]/T H-H°(Tr) fH° fG° log Kf
0              
100              
200              
 
298.15 128.574 172.412 172.412 0. -2046.329 -1946.752 341.063
 
300 129.026 173.209 172.415 0.238 -2046.338 -1946.134 338.852
400 146.285 212.948 177.716 14.093 -2046.150 -1912.729 249.777
500 156.410 246.751 188.230 29.260 -2045.173 -1879.476 196.347
 
600 163.686 275.939 200.472 45.280 -2043.833 -1846.458 160.748
700 169.582 301.626 213.124 61.952 -2042.303 -1813.681 135.339
800 174.707 324.612 225.648 79.171 -2040.658 -1781.133 116.296
900 179.360 345.462 237.820 96.877 -2038.991 -1748.792 101.497
1000 183.686 364.585 249.553 115.032 -2054.594 -1715.209 89.593
 
1100 187.778 382.286 260.825 133.607 -2053.214 -1681.336 79.840
1200 191.690 398.793 271.642 152.581 -2055.694 -1647.475 71.713
1300 195.456 414.286 282.025 171.940 -2053.344 -1613.550 64.833
1400 199.091 428.905 291.999 191.668 -2305.581 -1573.481 58.707
 
1400.000 199.091 428.905 291.999 191.668 GLASS <--> LIQUID
1400.000 228.446 428.905 291.999 191.668 TRANSITION
 
1500 228.446 444.666 301.658 214.513 -2297.326 -1521.477 52.983
 
1600 228.446 459.410 311.061 237.357 -2289.228 -1470.019 47.991
1700 228.446 473.259 320.199 260.202 -2281.297 -1419.062 43.602
1800 228.446 486.317 329.069 283.047 -2273.545 -1368.568 39.715
1900 228.446 498.668 337.673 305.891 -2265.985 -1318.498 36.248
2000 228.446 510.386 346.018 328.736 -2273.315 -1268.368 33.126
 
 
2013.000 228.446 511.866 347.084 331.706 CRYSTAL <--> LIQUID
 
2100 228.446 521.532 354.113 351.580 2266.923 1218.278 30.303
2200 228.446 532.159 361.966 374.425 -2260.577 -1168.490 27.743
2300 228.446 542.314 369.588 397.270 -2254.277 -1118.992 25.413
2400 228.446 552.037 376.989 420.114 -2248.023 -1069.766 23.283
2500 228.446 561.362 384.179 442.959 -2241.816 -1020.800 21.328
 
2600 228.446 570.322 391.167 465.804 -2235.654 -972.081 19.529
2700 228.446 578.944 397.963 488.648 -2229.540 -923.598 17.868
2800 228.446 587.252 404.576 511.493 -2223.473 -875.340 16.330
2900 228.446 595.268 411.014 534.338 -2217.453 -827.300 14.901
3000 228.446 603.013 417.286 557.182 -2211.483 -779.465 13.572
 
3100 228.446 610.504 423.398 580.027 -2205.563 -731.828 12.331
3200 228.446 617.757 429.359 602.872 -2199.695 -684.383 11.171
3300 228.446 624.786 435.175 625.716 -2193.881 -637.120 10.085
3400 228.446 631.606 440.853 648.561 -2188.122 -590.031 9.065
3500 228.446 638.228 446.398 671.405 -2182.422 -543.113 8.106
 
3600 228.446 644.664 451.817 694.250 -2176.783 -496.355 7.202
3700 228.446 650.923 457.114 717.095 -2580.306 -441.966 6.239
3800 228.446 657.015 462.294 739.939 -2573.563 -384.261 5.282
3900 228.446 662.949 467.364 762.784 -2566.947 -326.734 4.376
4000 228.446 668.733 472.326 785.629 -2560.458 -269.377 3.518
 
PREVIOUS: June 1961 CURRENT: June 1967
 
Magnesium Titanium Oxide (Mg2TiO4) Mg2O4Ti1(l)

Download table in tab-delimited text format.