Titanium Nitride (TiN) N1Ti1(l)
 
Enthalpy Reference Temperature = Tr = 298.15 K Standard State Pressure = p° = 0.1 MPa
  J·K-1 mol-1 kJ·mol-1  
T/K Cp° S° -[G°-H°(Tr)]/T H-H°(Tr) fH° fG° log Kf
0              
100              
200              
 
298.15 37.079 52.733 52.733 0. -265.813 -243.800 42.713
 
300 37.238 52.963 52.734 0.069 -265.818 -243.664 42.426
400 43.811 64.670 54.285 4.154 -265.805 -236.267 30.853
500 47.057 74.836 57.404 8.716 -265.453 -228.919 23.915
 
600 48.723 83.572 61.056 13.510 -264.976 -221.656 19.297
700 49.781 91.165 64.827 18.437 -264.458 -214.477 16.004
800 50.618 97.868 68.546 23.458 -263.917 -207.374 13.540
900 51.384 103.874 72.143 28.558 -263.396 -200.337 11.627
1000 52.145 109.327 75.593 33.734 -262.961 -193.355 10.100
 
1100 52.919 114.333 78.891 38.987 -262.672 -186.410 8.852
1200 53.718 118.972 82.040 44.319 -266.509 -179.365 7.808
1300 54.538 123.304 85.049 49.731 -265.774 -172.133 6.916
1400 55.384 127.377 87.929 55.227 -265.054 -164.957 6.155
1500 56.246 131.227 90.688 60.809 -264.357 -157.831 5.496
 
1600 57.128 134.885 93.337 66.477 -263.692 -150.751 4.922
1700 58.020 138.375 95.884 72.235 -263.070 -143.712 4.416
1800 58.927 141.717 98.338 78.082 -262.501 -136.708 3.967
1900 59.848 144.928 100.706 84.020 -261.995 -129.733 3.567
2000 60.777 148.021 102.995 90.052 -276.251 -122.330 3.195
 
2100 61.710 151.009 105.211 96.176 -276.653 -114.624 2.851
2200 62.655 153.901 107.359 102.394 -276.968 -106.900 2.538
 
2200.000 62.655 153.901 107.359 102.394 GLASS <--> LIQUID
2200.000 62.760 153.901 107.359 102.394 TRANSITION
 
2300 62.760 156.691 109.443 108.670 -277.232 -99.164 2.252
2400 62.760 159.362 111.468 114.946 -277.503 -91.416 1.990
2500 62.760 161.924 113.436 121.222 -277.779 -83.657 1.748
 
2600 62.760 164.386 115.348 127.498 -278.060 -75.886 1.525
2700 62.760 166.754 117.208 133.774 -278.345 -68.105 1.318
2800 62.760 169.037 119.019 140.050 -278.635 -60.313 1.125
2900 62.760 171.239 120.782 146.326 -278.929 -52.511 0.946
3000 62.760 173.367 122.499 152.602 -279.227 -44.698 0.778
 
3100 62.760 175.425 124.174 158.878 -279.527 -36.876 0.621
3200 62.760 177.417 125.807 165.154 -279.832 -29.043 0.474
 
3220.000 62.760 177.808 126.128 166.409 CRYSTAL <--> LIQUID
 
3300 62.760 179.348 127.400 171.430 280.139 21.201 0.336
3400 62.760 181.222 128.956 177.706 -280.449 -13.350 0.205
3500 62.760 183.041 130.475 183.982 -280.761 -5.490 0.082
 
3600 62.760 184.809 131.960 190.258 -281.076 2.379 -0.035
3700 62.760 186.529 133.412 196.534 -690.492 18.046 -0.255
3800 62.760 188.203 134.832 202.810 -689.578 37.183 -0.511
3900 62.760 189.833 136.221 209.086 -688.721 56.297 -0.754
4000 62.760 191.422 137.581 215.362 -687.920 75.390 -0.984
 
4100 62.760 192.971 138.913 221.638 -687.174 94.463 -1.203
4200 62.760 194.484 140.219 227.914 -686.481 113.519 -1.412
4300 62.760 195.961 141.498 234.190 -685.839 132.559 -1.610
4400 62.760 197.403 142.752 240.466 -685.247 151.585 -1.800
4500 62.760 198.814 143.982 246.742 -684.701 170.597 -1.980
 
PREVIOUS: December 1960 CURRENT: June 1968
 
Titanium Nitride (TiN) N1Ti1(l)

Download table in tab-delimited text format.