fH°fG°| Titanium Oxide, Alpha (TiO) | O1Ti1(cr) | |||||||||||||
| Enthalpy Reference Temperature = Tr = 298.15 K | Standard State Pressure = p° = 0.1 MPa | |||||||||||||
| J·K-1 mol-1 | kJ·mol-1 | |||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| T/K | Cp° | S° | -[G°-H°(Tr)]/T | H-H°(Tr) | fH° |
fG° |
log Kf | |||||||
| 0 | 0.000 | 0.000 | INFINITE | -6.174 | -539.668 | -539.668 | INFINITE | |||||||
| 100 | 12.765 | 5.732 | 63.375 | -5.764 | -541.270 | -532.352 | 278.072 | |||||||
| 200 | 30.681 | 20.585 | 38.164 | -3.516 | -542.394 | -522.918 | 136.572 | |||||||
| 298.15 | 39.957 | 34.769 | 34.769 | 0.000 | -542.665 | -513.278 | 89.924 | |||||||
| 300 | 40.062 | 35.017 | 34.770 | 0.074 | -542.665 | -513.096 | 89.338 | |||||||
| 400 | 44.978 | 47.274 | 36.408 | 4.346 | -542.491 | -503.257 | 65.719 | |||||||
| 500 | 48.242 | 57.679 | 39.648 | 9.015 | -542.092 | -493.491 | 51.555 | |||||||
| 600 | 50.836 | 66.709 | 43.422 | 13.972 | -541.541 | -483.821 | 42.120 | |||||||
| 700 | 53.095 | 74.719 | 47.331 | 19.171 | -540.857 | -474.253 | 35.389 | |||||||
| 800 | 55.187 | 81.947 | 51.214 | 24.586 | -540.035 | -464.793 | 30.348 | |||||||
| 900 | 57.153 | 88.561 | 55.001 | 30.204 | -539.111 | -455.442 | 26.433 | |||||||
| 1000 | 59.078 | 94.682 | 58.667 | 36.016 | -538.152 | -446.197 | 23.307 | |||||||
| 1100 | 60.961 | 100.402 | 62.203 | 42.018 | -537.219 | -437.047 | 20.754 | |||||||
| 1200 | 62.802 | 105.785 | 65.613 | 48.206 | -540.300 | -427.861 | 18.624 | |||||||
| 1265.000 | 63.998 | 109.129 | 67.764 | 52.327 | ALPHA <--> BETA | |||||||||
| 1300 | 64.643 | 110.884 | 68.901 | 54.578 | 538.700 418.555 16.818 | |||||||||
| 1400 | 66.442 | 115.741 | 72.075 | 61.133 | -537.011 | -409.376 | 15.274 | |||||||
| 1500 | 68.241 | 120.386 | 75.142 | 67.867 | -535.248 | -400.320 | 13.940 | |||||||
| 1600 | 70.040 | 124.848 | 78.110 | 74.781 | -533.422 | -391.384 | 12.777 | |||||||
| 1700 | 71.839 | 129.148 | 80.986 | 81.875 | -531.546 | -382.564 | 11.755 | |||||||
| 1800 | 73.597 | 133.304 | 83.778 | 89.147 | -529.636 | -373.856 | 10.849 | |||||||
| 1900 | 75.396 | 137.331 | 86.491 | 96.597 | -527.704 | -365.254 | 10.042 | |||||||
| 2000 | 77.153 | 141.243 | 89.131 | 104.224 | -540.450 | -356.300 | 9.306 | |||||||
| 2100 | 78.910 | 145.050 | 91.704 | 112.027 | -539.263 | -347.121 | 8.634 | |||||||
| 2200 | 80.668 | 148.762 | 94.214 | 120.006 | -537.912 | -338.002 | 8.025 | |||||||
| 2300 | 82.467 | 152.387 | 96.664 | 128.163 | -536.394 | -328.949 | 7.471 | |||||||
| 2400 | 84.224 | 155.934 | 99.060 | 136.497 | -534.710 | -319.965 | 6.964 | |||||||
| 2500 | 85.981 | 159.408 | 101.405 | 145.007 | -532.861 | -311.055 | 6.499 | |||||||
| PREVIOUS: March 1967 | CURRENT: December 1973 | |||||||||||||
| Titanium Oxide, Alpha (TiO) | O1Ti1(cr) | |||||||||||||