Titanium Oxide, Beta (TiO) O1Ti1(cr)
 
Enthalpy Reference Temperature = Tr = 298.15 K Standard State Pressure = p° = 0.1 MPa
  J·K-1 mol-1 kJ·mol-1  
T/K Cp° S° -[G°-H°(Tr)]/T H-H°(Tr) fH° fG° log Kf
0              
100              
200              
 
298.15 39.957 38.077 38.077 0.000 -538.481 -510.080 89.364
 
300 40.062 38.324 38.078 0.074 -538.480 -509.904 88.782
400 44.978 50.582 39.715 4.346 -538.307 -500.396 65.345
500 48.242 60.987 42.956 9.015 -537.908 -490.961 51.290
 
600 50.836 70.016 46.730 13.972 -537.356 -481.621 41.929
700 53.095 78.026 50.639 19.171 -536.673 -472.384 35.250
800 55.187 85.254 54.521 24.586 -535.851 -463.255 30.247
900 57.153 91.868 58.309 30.204 -534.927 -454.235 26.363
1000 59.078 97.990 61.974 36.016 -533.967 -445.321 23.261
 
1100 60.961 103.709 65.511 42.018 -533.035 -436.501 20.728
1200 62.802 109.093 68.921 48.206 -536.116 -427.646 18.615
 
1265.000 64.013 112.436 71.071 52.327 ALPHA <--> BETA
 
1300 64.643 114.192 72.209 54.578 534.515 418.671 16.822
1400 66.442 119.048 75.382 61.133 -532.827 -409.822 15.291
1500 68.241 123.694 78.449 67.867 -531.063 -401.098 13.967
 
1600 70.040 128.155 81.417 74.781 -529.238 -392.492 12.814
1700 71.839 132.456 84.294 81.875 -527.362 -384.003 11.799
1800 73.597 136.612 87.086 89.147 -525.452 -375.625 10.900
1900 75.396 140.639 89.799 96.597 -523.520 -367.354 10.099
2000 77.153 144.551 92.439 104.224 -536.265 -358.732 9.369
 
 
2023.000 77.551 145.436 93.037 106.003 BETA <--> LIQUID
 
2100 78.910 148.358 95.012 112.027 535.079 349.883 8.703
2200 80.668 152.069 97.521 120.006 -533.728 -341.095 8.099
2300 82.467 155.695 99.972 128.163 -532.210 -332.373 7.548
2400 84.224 159.242 102.368 136.497 -530.526 -323.720 7.046
2500 85.981 162.716 104.713 145.008 -528.677 -315.140 6.584
 
PREVIOUS: March 1967 CURRENT: December 1973
 
Titanium Oxide, Beta (TiO) O1Ti1(cr)

Download table in tab-delimited text format.