Titanium Oxide (TiO)								O1Ti1(l)
Enthalpy Reference Temperature = Tr = 298.15 K								Standard State Pressure = p° = 0.1 MPa
		J·K-1 mol-1						kJ·mol-1
T/K		Cp°		S°		-[G°-H°(Tr)]/T		H-H°(Tr)		fH°		fG°		log Kf
0
100
200
298.15		39.957		60.140		60.140		0.000		-493.939		-472.116		82.713
300		40.062		60.387		60.140		0.074		-493.938		-471.981		82.179
400		44.978		72.644		61.778		4.346		-493.765		-464.679		60.681
500		48.242		83.049		65.018		9.015		-493.366		-457.450		47.790
600		50.836		92.079		68.792		13.972		-492.814		-450.317		39.204
700		53.095		100.089		72.702		19.171		-492.131		-443.286		33.078
800		55.187		107.317		76.584		24.586		-491.309		-436.363		28.492
900		57.153		113.931		80.371		30.204		-490.385		-429.549		24.930
1000		59.078		120.053		84.037		36.016		-489.425		-422.841		22.087
1100		60.961		125.772		87.574		42.018		-488.493		-416.229		19.765
1200		62.802		131.156		90.984		48.206		-491.573		-409.579		17.829
1200.000		62.802		131.156		90.984		48.206		GLASS <--> LIQUID
1200.000		66.944		131.156		90.984		48.206		TRANSITION
1300		66.944		136.514		94.283		54.901		-489.651		-402.825		16.186
1400		66.944		141.475		97.479		61.595		-487.822		-396.215		14.783
1500		66.944		146.094		100.567		68.290		-486.098		-389.733		13.572
1600		66.944		150.414		103.549		74.984		-484.492		-383.361		12.515
1700		66.944		154.473		106.427		81.678		-483.016		-377.086		11.586
1800		66.944		158.299		109.203		88.373		-481.684		-370.895		10.763
1900		66.944		161.919		111.883		95.067		-480.507		-364.772		10.028
2000		66.944		165.352		114.472		101.762		-494.186		-358.254		9.357
2023.000		66.944		166.118		115.054		103.301		BETA <--> LIQUID
2100		66.944		168.619		116.973		108.456		494.108 351.460 8.742
2200		66.944		171.733		119.392		115.150		-494.041		-344.668		8.183
2300		66.944		174.709		121.733		121.845		-493.986		-337.880		7.673
2400		66.944		177.558		124.000		128.539		-493.942		-331.094		7.206
2500		66.944		180.291		126.197		135.234		-493.909		-324.309		6.776
2600		66.944		182.916		128.328		141.928		-493.886		-317.526		6.379
2700		66.944		185.443		130.397		148.622		-493.874		-310.743		6.012
2800		66.944		187.877		132.407		155.317		-493.872		-303.960		5.670
2900		66.944		190.226		134.360		162.011		-493.880		-297.178		5.353
3000		66.944		192.496		136.261		168.706		-493.898		-290.395		5.056
3100		66.944		194.691		138.110		175.400		-493.925		-283.611		4.779
3200		66.944		196.816		139.912		182.094		-493.962		-276.826		4.519
3300		66.944		198.876		141.668		188.789		-494.006		-270.040		4.274
3400		66.944		200.875		143.380		195.483		-494.060		-263.252		4.044
3500		66.944		202.815		145.050		202.178		-494.121		-256.463		3.828
3600		66.944		204.701		146.681		208.872		-494.190		-249.672		3.623
3700		66.944		206.535		148.274		215.566		-903.365		-235.090		3.319
3800		66.944		208.321		149.831		222.261		-902.214		-217.044		2.983
3900		66.944		210.060		151.353		228.955		-901.125		-199.027		2.666
4000		66.944		211.754		152.842		235.650		-900.098		-181.038		2.364
4100		66.944		213.407		154.299		242.344		-899.129		-163.074		2.078
4200		66.944		215.021		155.726		249.038		-898.218		-145.133		1.805
4300		66.944		216.596		157.123		255.733		-897.362		-127.212		1.545
4400		66.944		218.135		158.492		262.427		-896.559		-109.311		1.298
4500		66.944		219.639		159.835		269.122		-895.809		-91.428		1.061
PREVIOUS: March 1967								CURRENT: December 1973
Titanium Oxide (TiO)								O1Ti1(l)

Download table in tab-delimited text format.