Titanium Oxide (TiO) O1Ti1(cr,l)
 
Enthalpy Reference Temperature = Tr = 298.15 K Standard State Pressure = p° = 0.1 MPa
  J·K-1 mol-1 kJ·mol-1  
T/K Cp° S° -[G°-H°(Tr)]/T H-H°(Tr) fH° fG° log Kf
0 0.000 0.000 INFINITE -6.174 -539.668 -539.668 INFINITE
100 12.765 5.732 63.375 -5.764 -541.270 -532.352 278.072
200 30.681 20.585 38.164 -3.516 -542.394 -522.918 136.572
 
298.15 39.957 34.769 34.769 0.000 -542.665 -513.278 89.924
 
300 40.062 35.017 34.770 0.074 -542.665 -513.096 89.338
400 44.978 47.274 36.408 4.346 -542.491 -503.257 65.719
500 48.242 57.679 39.648 9.015 -542.092 -493.491 51.555
 
600 50.836 66.709 43.422 13.972 -541.541 -483.821 42.120
700 53.095 74.719 47.331 19.171 -540.857 -474.253 35.389
800 55.187 81.947 51.214 24.586 -540.035 -464.793 30.348
900 57.153 88.561 55.001 30.204 -539.111 -455.442 26.433
1000 59.078 94.682 58.667 36.016 -538.152 -446.197 23.307
 
1100 60.961 100.402 62.203 42.018 -537.219 -437.047 20.754
1200 62.802 105.785 65.613 48.206 -540.300 -427.861 18.624
 
1265.000 63.998 109.129 67.764 52.327 ALPHA <--> BETA
1265.000 64.013 112.436 67.764 56.511 TRANSITION
 
1300 64.643 114.192 68.990 58.763 -534.515 -418.671 16.822
1400 66.442 119.048 72.394 65.317 -532.827 -409.822 15.291
1500 68.241 123.694 75.660 72.051 -531.063 -401.098 13.967
 
1600 70.040 128.155 78.802 78.965 -529.238 -392.492 12.814
1700 71.839 132.456 81.833 86.059 -527.362 -384.003 11.799
1800 73.597 136.612 84.761 93.331 -525.452 -375.625 10.900
1900 75.396 140.639 87.597 100.781 -523.520 -367.354 10.099
2000 77.153 144.551 90.347 108.409 -536.265 -358.731 9.369
 
 
2023.000 77.551 145.436 90.968 110.188 BETA <--> LIQUID
2023.000 66.944 166.118 90.968 152.028 TRANSITION
 
2100 66.944 168.619 93.770 157.182 -494.108 -351.460 8.742
2200 66.944 171.733 97.243 163.877 -494.041 -344.668 8.183
2300 66.944 174.709 100.547 170.571 -493.986 -337.880 7.673
2400 66.944 177.558 103.697 177.266 -493.942 -331.094 7.206
2500 66.944 180.291 106.707 183.960 -493.909 -324.309 6.776
 
2600 66.944 182.916 109.588 190.654 -493.886 -317.526 6.379
2700 66.944 185.443 112.351 197.349 -493.874 -310.743 6.012
2800 66.944 187.877 115.005 204.043 -493.872 -303.960 5.670
2900 66.944 190.226 117.558 210.738 -493.880 -297.178 5.353
3000 66.944 192.496 120.019 217.432 -493.898 -290.395 5.056
 
3100 66.944 194.691 122.392 224.126 -493.925 -283.611 4.779
3200 66.944 196.816 124.685 230.821 -493.962 -276.826 4.519
3300 66.944 198.876 126.902 237.515 -494.006 -270.040 4.274
3400 66.944 200.875 129.048 244.210 -494.060 -263.252 4.044
3500 66.944 202.815 131.129 250.904 -494.121 -256.463 3.828
 
3600 66.944 204.701 133.146 257.598 -494.190 -249.672 3.623
3700 66.944 206.535 135.105 264.293 -903.365 -235.090 3.319
3800 66.944 208.321 137.008 270.987 -902.214 -217.044 2.983
3900 66.944 210.060 138.859 277.682 -901.125 -199.027 2.666
4000 66.944 211.754 140.661 284.376 -900.098 -181.038 2.364
 
4100 66.944 213.408 142.415 291.070 -899.129 -163.074 2.078
4200 66.944 215.021 144.124 297.765 -898.218 -145.133 1.805
4300 66.944 216.596 145.791 304.459 -897.362 -127.212 1.545
4400 66.944 218.135 147.418 311.154 -896.559 -109.311 1.298
4500 66.944 219.639 149.006 317.848 -895.809 -91.428 1.061
 