Vanadium Oxide (VO)								O1V1(l)
Enthalpy Reference Temperature = Tr = 298.15 K								Standard State Pressure = p° = 0.1 MPa
		J·K-1 mol-1						kJ·mol-1
T/K		Cp°		S°		-[G°-H°(Tr)]/T		H-H°(Tr)		fH°		fG°		log Kf
0
100
200
298.15		45.501		69.137		69.137		0.000		-370.901		-352.304		61.722
300		45.647		69.419		69.138		0.084		-370.890		-352.189		61.322
400		49.580		83.188		70.988		4.880		-370.144		-346.062		45.191
500		51.651		94.481		74.592		9.945		-369.269		-340.141		35.534
600		53.530		104.066		78.725		15.204		-368.311		-334.403		29.112
700		55.343		112.454		82.956		20.648		-367.270		-328.833		24.538
800		57.099		119.959		87.121		26.271		-366.149		-323.418		21.117
900		58.803		126.783		91.154		32.067		-364.958		-318.147		18.465
1000		60.463		133.065		95.035		38.030		-363.698		-313.013		16.350
1100		62.086		138.904		98.761		44.158		-362.371		-308.008		14.626
1200		63.676		144.375		102.336		50.446		-360.991		-303.127		13.195
1200.000		63.676		144.375		102.336		50.446		GLASS <--> LIQUID
1200.000		62.760		144.375		102.336		50.446		TRANSITION
1300		62.760		149.399		105.766		56.722		-359.733		-298.357		11.988
1400		62.760		154.050		109.051		62.998		-358.591		-293.679		10.957
1500		62.760		158.380		112.197		69.274		-357.566		-289.079		10.067
1600		62.760		162.430		115.211		75.550		-356.656		-284.543		9.289
1700		62.760		166.235		118.102		81.826		-355.870		-280.061		8.605
1800		62.760		169.822		120.876		88.102		-355.212		-275.621		7.998
1900		62.760		173.215		123.542		94.378		-354.693		-271.214		7.456
2000		62.760		176.434		126.107		100.654		-354.319		-266.831		6.969
2063.000		62.760		178.381		127.674		104.608		CRYSTAL <--> LIQUID
2100		62.760		179.497		128.577		106.930		354.103 262.463 6.528
2200		62.760		182.416		130.959		113.206		-376.933		-257.996		6.126
2300		62.760		185.206		133.257		119.482		-377.193		-252.584		5.736
2400		62.760		187.877		135.478		125.758		-377.464		-247.161		5.379
2500		62.760		190.439		137.625		132.034		-377.745		-241.726		5.051
2600		62.760		192.900		139.704		138.310		-378.038		-236.279		4.747
2700		62.760		195.269		141.719		144.586		-378.341		-230.821		4.466
2800		62.760		197.551		143.672		150.862		-378.654		-225.352		4.204
2900		62.760		199.754		145.568		157.138		-378.977		-219.871		3.960
3000		62.760		201.881		147.410		163.414		-379.310		-214.379		3.733
3100		62.760		203.939		149.201		169.690		-379.652		-208.875		3.520
3200		62.760		205.932		150.942		175.966		-380.004		-203.361		3.320
3300		62.760		207.863		152.638		182.242		-380.364		-197.836		3.131
3400		62.760		209.737		154.290		188.518		-380.732		-192.299		2.954
3500		62.760		211.556		155.900		194.794		-381.108		-186.751		2.787
PREVIOUS:								CURRENT: December 1973
Vanadium Oxide (VO)								O1V1(l)

Download table in tab-delimited text format.