Vanadium Oxide (VO) O1V1(l) T(K) Cp S -[G-H(Tr)]/T H-H(Tr) delta-f H delta-f G log Kf 0 100 200 298.15 45.501 69.137 69.137 0.000 -370.901 -352.304 61.722 300 45.647 69.419 69.138 0.084 -370.890 -352.189 61.322 400 49.580 83.188 70.988 4.880 -370.144 -346.062 45.191 500 51.651 94.481 74.592 9.945 -369.269 -340.141 35.534 600 53.530 104.066 78.725 15.204 -368.311 -334.403 29.112 700 55.343 112.454 82.956 20.648 -367.270 -328.833 24.538 800 57.099 119.959 87.121 26.271 -366.149 -323.418 21.117 900 58.803 126.783 91.154 32.067 -364.958 -318.147 18.465 1000 60.463 133.065 95.035 38.030 -363.698 -313.013 16.350 1100 62.086 138.904 98.761 44.158 -362.371 -308.008 14.626 1200 63.676 144.375 102.336 50.446 -360.991 -303.127 13.195 1200.000 63.676 144.375 102.336 50.446 GLASS <--> LIQUID 1200.000 62.760 144.375 102.336 50.446 TRANSITION 1300 62.760 149.399 105.766 56.722 -359.733 -298.357 11.988 1400 62.760 154.050 109.051 62.998 -358.591 -293.679 10.957 1500 62.760 158.380 112.197 69.274 -357.566 -289.079 10.067 1600 62.760 162.430 115.211 75.550 -356.656 -284.543 9.289 1700 62.760 166.235 118.102 81.826 -355.870 -280.061 8.605 1800 62.760 169.822 120.876 88.102 -355.212 -275.621 7.998 1900 62.760 173.215 123.542 94.378 -354.693 -271.214 7.456 2000 62.760 176.434 126.107 100.654 -354.319 -266.831 6.969 2063.000 62.760 178.381 127.674 104.608 CRYSTAL <--> LIQUID 2100 62.760 179.497 128.577 106.930 354.103 262.463 6.528 2200 62.760 182.416 130.959 113.206 -376.933 -257.996 6.126 2300 62.760 185.206 133.257 119.482 -377.193 -252.584 5.736 2400 62.760 187.877 135.478 125.758 -377.464 -247.161 5.379 2500 62.760 190.439 137.625 132.034 -377.745 -241.726 5.051 2600 62.760 192.900 139.704 138.310 -378.038 -236.279 4.747 2700 62.760 195.269 141.719 144.586 -378.341 -230.821 4.466 2800 62.760 197.551 143.672 150.862 -378.654 -225.352 4.204 2900 62.760 199.754 145.568 157.138 -378.977 -219.871 3.960 3000 62.760 201.881 147.410 163.414 -379.310 -214.379 3.733 3100 62.760 203.939 149.201 169.690 -379.652 -208.875 3.520 3200 62.760 205.932 150.942 175.966 -380.004 -203.361 3.320 3300 62.760 207.863 152.638 182.242 -380.364 -197.836 3.131 3400 62.760 209.737 154.290 188.518 -380.732 -192.299 2.954 3500 62.760 211.556 155.900 194.794 -381.108 -186.751 2.787