		J·K^-1 mol^-1						kJ·mol^-1
Vanadium Oxide (VO)								O₁V₁(cr,l)

Enthalpy Reference Temperature = T_r = 298.15 K								Standard State Pressure = p° = 0.1 MPa
T/K		C_p^°		S^°		-[G^°-H^°(T_r)]/T		H-H^°(T_r)		_fH^°		_fG^°		log K_f
0		0.000		0.000		INFINITE		-6.908		-429.715		-429.715		INFINITE
100		13.895		6.730		71.088		-6.436		-431.184		-422.473		220.677
200		34.100		23.035		42.859		-3.965		-432.005		-413.352		107.956

298.15		45.501		39.011		39.011		0.000		-431.789		-404.210		70.816

300		45.647		39.293		39.012		0.084		-431.778		-404.039		70.350
400		49.580		53.063		40.863		4.880		-431.032		-394.899		51.569
500		51.651		64.356		44.466		9.945		-430.157		-385.966		40.322

600		53.530		73.940		48.599		15.204		-429.199		-377.216		32.840
700		55.343		82.329		52.831		20.648		-428.158		-368.633		27.508
800		57.099		89.834		56.995		26.271		-427.037		-360.206		23.519
900		58.803		96.658		61.029		32.067		-425.846		-351.922		20.425
1000		60.463		102.940		64.910		38.030		-424.586		-343.776		17.957

1100		62.086		108.779		68.635		44.158		-423.259		-335.758		15.944
1200		63.677		114.250		72.211		50.446		-421.879		-327.864		14.272
1300		65.243		119.408		75.645		56.892		-420.450		-320.087		12.861
1400		66.791		124.300		78.947		63.494		-418.983		-312.422		11.657
1500		68.325		128.961		82.127		70.250		-417.478		-304.863		10.616

1600		69.842		133.419		85.195		77.159		-415.936		-297.405		9.709
1700		71.351		137.698		88.158		84.218		-414.366		-290.045		8.912
1800		72.851		141.819		91.025		91.429		-412.774		-282.778		8.206
1900		74.339		145.798		93.804		98.788		-411.171		-275.599		7.577
2000		75.847		149.649		96.500		106.297		-409.565		-268.506		7.013


2063.000		76.747		152.015		98.160		111.104		CRYSTAL <--> LIQUID
2063.000		62.760		178.381		98.160		165.496		TRANSITION

2100		62.760		179.497		99.583		167.818		-354.103		-262.463		6.528
2200		62.760		182.416		103.282		174.094		-376.933		-257.996		6.126
2300		62.760		185.206		106.784		180.370		-377.193		-252.584		5.736
2400		62.760		187.877		110.108		186.646		-377.464		-247.161		5.379
2500		62.760		190.439		113.270		192.922		-377.745		-241.726		5.051

2600		62.760		192.900		116.286		199.198		-378.038		-236.279		4.747
2700		62.760		195.269		119.167		205.474		-378.341		-230.821		4.466
2800		62.760		197.551		121.926		211.750		-378.654		-225.352		4.204
2900		62.760		199.754		124.572		218.026		-378.977		-219.871		3.960
3000		62.760		201.881		127.114		224.302		-379.310		-214.379		3.733

3100		62.760		203.939		129.559		230.578		-379.652		-208.875		3.520
3200		62.760		205.932		131.915		236.854		-380.004		-203.361		3.320
3300		62.760		207.863		134.187		243.130		-380.364		-197.836		3.131
3400		62.760		209.737		136.382		249.406		-380.732		-192.299		2.954
3500		62.760		211.556		138.504		255.682		-381.108		-186.751		2.787

PREVIOUS:								CURRENT: December 1973

Vanadium Oxide (VO)								O₁V₁(cr,l)