Titanium Oxide (TiO2)								O2Ti1(l)
Enthalpy Reference Temperature = Tr = 298.15 K								Standard State Pressure = p° = 0.1 MPa
		J·K-1 mol-1						kJ·mol-1
T/K		Cp°		S°		-[G°-H°(Tr)]/T		H-H°(Tr)		fH°		fG°		log Kf
0
100
200
298.15		55.103		72.345		72.345		0.000		-894.055		-845.289		148.091
300		55.287		72.686		72.346		0.102		-894.054		-844.987		147.125
400		62.835		89.724		74.617		6.043		-893.698		-828.670		108.213
500		67.203		104.254		79.130		12.562		-892.978		-812.492		84.880
600		69.931		116.765		84.384		19.429		-892.097		-796.475		69.339
700		71.764		127.691		89.807		26.519		-891.149		-780.613		58.250
800		73.078		137.364		95.159		33.764		-890.166		-764.889		49.942
900		74.057		146.030		100.338		41.122		-889.204		-749.288		43.488
1000		74.852		153.875		105.306		48.569		-888.340		-733.789		38.329
1100		75.479		161.039		110.052		56.086		-887.647		-718.369		34.113
1200		76.023		167.630		114.579		63.662		-891.115		-702.884		30.596
1300		76.525		173.736		118.897		71.290		-890.050		-687.242		27.614
1400		76.944		179.423		123.020		78.964		-889.049		-671.679		25.061
1400.000		76.944		179.423		123.020		78.964		GLASS <--> LIQUID
1400.000		100.416		179.423		123.020		78.964		TRANSITION
1500		100.416		186.351		127.014		89.006		-885.798		-656.268		22.853
1600		100.416		192.832		130.927		99.047		-882.679		-641.068		20.929
1700		100.416		198.919		134.749		109.089		-879.701		-626.059		19.236
1800		100.416		204.659		138.475		119.131		-876.879		-611.221		17.737
1900		100.416		210.088		142.103		129.172		-874.225		-596.536		16.400
2000		100.416		215.239		145.632		139.214		-886.438		-581.532		15.188
2100		100.416		220.138		149.064		149.255		-884.906		-566.324		14.087
2130.000		100.416		221.563		150.075		152.268		CRYSTAL <--> LIQUID
2200		100.416		224.809		152.402		159.297		883.396 551.189 13.087
2300		100.416		229.273		155.648		169.339		-881.909		-536.122		12.176
2400		100.416		233.547		158.805		179.380		-880.444		-521.120		11.342
2500		100.416		237.646		161.877		189.422		-879.001		-506.177		10.576
2600		100.416		241.584		164.868		199.463		-877.579		-491.293		9.870
2700		100.416		245.374		167.780		209.505		-876.179		-476.462		9.218
2800		100.416		249.026		170.617		219.547		-874.799		-461.682		8.613
2900		100.416		252.550		173.381		229.588		-873.438		-446.953		8.050
3000		100.416		255.954		176.077		239.630		-872.098		-432.269		7.526
3100		100.416		259.247		178.707		249.671		-870.775		-417.630		7.037
3200		100.416		262.435		181.274		259.713		-869.471		-403.034		6.579
3300		100.416		265.525		183.781		269.755		-868.184		-388.478		6.149
3400		100.416		268.522		186.229		279.796		-866.914		-373.960		5.745
3500		100.416		271.433		188.622		289.838		-865.660		-359.480		5.365
3600		100.416		274.262		190.962		299.879		-864.422		-345.035		5.006
3700		100.416		277.013		193.251		309.921		-1272.296		-322.836		4.558
3800		100.416		279.691		195.491		319.963		-1269.853		-297.207		4.085
3900		100.416		282.300		197.683		330.004		-1267.478		-271.642		3.638
4000		100.416		284.842		199.830		340.046		-1265.171		-246.138		3.214
PREVIOUS: September 1966								CURRENT: December 1973
Titanium Oxide (TiO2)								O2Ti1(l)

Download table in tab-delimited text format.