Zirconium Oxide (ZrO2)								O2Zr1(cr)
Enthalpy Reference Temperature = Tr = 298.15 K								Standard State Pressure = p° = 0.1 MPa
		J·K-1 mol-1						kJ·mol-1
T/K		Cp°		S°		-[G°-H°(Tr)]/T		H-H°(Tr)		fH°		fG°		log Kf
0		0.000		0.000		INFINITE		-8.749		-1092.032		-1092.032		INFINITE
100		18.927		9.488		90.390		-8.090		-1095.164		-1077.376		562.764
200		42.778		30.546		55.114		-4.914		-1097.091		-1058.694		276.502
298.15		56.191		50.359		50.359		0.000		-1097.463		-1039.724		182.155
300		56.262		50.707		50.360		0.104		-1097.460		-1039.366		180.970
400		63.848		68.064		52.675		6.155		-1096.940		-1020.063		133.207
500		67.764		82.769		57.264		12.753		-1096.026		-1000.945		104.568
600		70.237		95.356		62.589		19.660		-1094.969		-982.027		85.493
700		72.023		106.323		68.070		26.777		-1093.873		-963.289		71.882
800		73.450		116.036		73.471		34.053		-1092.785		-944.709		61.683
900		74.663		124.759		78.693		41.459		-1091.731		-926.264		53.759
1000		75.747		132.682		83.702		48.981		-1090.727		-907.933		47.426
1100		76.743		139.949		88.489		56.606		-1089.783		-889.699		42.248
1200		77.684		146.667		93.061		64.327		-1092.612		-871.328		37.928
1300		78.580		152.921		97.428		72.141		-1091.250		-852.942		34.272
1400		79.450		158.776		101.603		80.042		-1089.872		-834.662		31.142
1478.000		80.108		163.101		104.735		86.265		I <--> II
1478.000		74.475		167.121		104.735		92.207		TRANSITION
1500		74.475		168.222		105.658		93.845		-1082.674		-816.569		28.435
1600		74.475		173.028		109.720		101.293		-1081.921		-798.854		26.080
1700		74.475		177.543		113.578		108.740		-1081.266		-781.183		24.003
1800		74.475		181.800		117.251		116.188		-1080.720		-763.547		22.158
1900		74.475		185.827		120.756		123.635		-1080.293		-745.939		20.507
2000		74.475		189.647		124.105		131.083		-1079.995		-728.349		19.023
2100		74.475		193.280		127.314		138.530		-1079.836		-710.772		17.679
2200		74.475		196.745		130.392		145.978		-1101.150		-692.452		16.441
2300		74.475		200.056		133.349		153.425		-1101.717		-673.863		15.304
2400		74.475		203.225		136.195		160.873		-1102.306		-655.248		14.261
2500		74.475		206.265		138.937		168.320		-1102.918		-636.608		13.301
2600		74.475		209.186		141.583		175.768		-1103.550		-617.943		12.415
2700		74.475		211.997		144.140		183.215		-1104.204		-599.253		11.593
2800		74.475		214.706		146.612		190.663		-1104.878		-580.539		10.830
2900		74.475		217.319		149.005		198.110		-1105.572		-561.801		10.119
2950.000		74.475		218.592		150.174		201.834		II <--> LIQUID
3000		74.475		219.844		151.325		205.558		1106.286 543.038 9.455
3100		74.475		222.286		153.575		213.005		-1107.018		-524.250		8.834
3200		74.475		224.650		155.759		220.453		-1107.768		-505.440		8.250
3300		74.475		226.942		157.881		227.900		-1108.536		-486.606		7.702
3400		74.475		229.165		159.945		235.348		-1109.320		-467.747		7.186
3500		74.475		231.324		161.954		242.795		-1110.120		-448.866		6.699
PREVIOUS: June 1961								CURRENT: December 1965
Zirconium Oxide (ZrO2)								O2Zr1(cr)

Download table in tab-delimited text format.