		J·K^-1 mol^-1						kJ·mol^-1
Lead Silicate (PbSiO₃)								O₃Pb₁Si₁(cr)

Enthalpy Reference Temperature = T_r = 298.15 K								Standard State Pressure = p° = 0.1 MPa
T/K		C_p^°		S^°		-[G^°-H^°(T_r)]/T		H-H^°(T_r)		_fH^°		_fG^°		log K_f
0		0.000		0.000		INFINITE		-16.219		-1138.091		-1138.091		INFINITE
100		44.683		37.168		177.245		-14.008		-1142.269		-1115.924		582.899
200		72.562		77.500		117.638		-8.028		-1144.359		-1088.626		284.320

298.15		90.040		109.927		109.927		0.000		-1144.993		-1061.094		185.899

300		90.333		110.485		109.929		0.167		-1144.995		-1060.574		184.662
400		102.843		138.266		113.631		9.854		-1144.615		-1032.467		134.826
500		111.964		162.238		121.011		20.614		-1143.535		-1004.544		104.944

600		118.742		183.282		129.672		32.166		-1141.987		-976.885		85.045
700		123.428		201.958		138.690		44.288		-1145.017		-948.711		70.794
800		126.566		218.655		147.661		56.795		-1143.041		-920.801		60.122
900		128.784		233.697		156.399		69.568		-1140.924		-893.146		51.837
1000		130.332		247.349		164.822		82.527		-1138.724		-865.733		45.221

1100		131.545		259.829		172.900		95.622		-1136.473		-838.542		39.819
1200		132.591		271.321		180.629		108.831		-1134.180		-811.559		35.326
1300		133.428		281.967		188.020		122.132		-1131.864		-784.767		31.532
1400		134.223		291.884		195.089		135.514		-1129.547		-758.154		28.287
1500		135.018		301.173		201.854		148.978		-1127.234		-731.708		25.480

1600		135.645		309.907		208.338		162.512		-1124.940		-705.414		23.029
1700		136.189		318.147		214.557		176.103		-1172.856		-678.816		20.857
1800		136.775		325.949		220.530		189.753		-1170.401		-649.826		18.857
1900		137.152		333.354		226.275		203.450		-1167.953		-620.972		17.072
2000		137.444		340.397		231.807		217.180		-1165.526		-592.246		15.468

PREVIOUS:								CURRENT: June 1965

Lead Silicate (PbSiO₃)								O₃Pb₁Si₁(cr)