		J·K^-1 mol^-1						kJ·mol^-1
Vanadium Oxide (V₂O₃)								O₃V₂(cr)

Enthalpy Reference Temperature = T_r = 298.15 K								Standard State Pressure = p° = 0.1 MPa
T/K		C_p^°		S^°		-[G^°-H^°(T_r)]/T		H-H^°(T_r)		_fH^°		_fG^°		log K_f
0		0.000		0.000		INFINITE		-17.476		-1213.971		-1213.971		INFINITE
100		28.627		14.163		179.288		-16.512		-1218.342		-1192.325		622.807

168.800		63.053		38.652		116.725		-13.179		I <--> II
168.800		63.136		48.269		116.725		-11.555		TRANSITION

200		80.107		60.767		107.019		-9.250		-1219.118		-1165.403		304.372

298.15		104.963		98.067		98.067		0.000		-1218.799		-1139.036		199.554

300		105.260		98.717		98.069		0.194		-1218.779		-1138.542		198.238
400		117.540		130.898		102.373		11.410		-1217.149		-1112.018		145.215
500		123.750		157.887		110.854		23.516		-1214.951		-1085.983		113.452

600		127.326		180.791		120.651		36.084		-1212.566		-1060.412		92.317
700		130.071		200.631		130.691		48.958		-1210.125		-1035.245		77.251
800		132.639		218.168		140.550		62.094		-1207.662		-1010.430		65.974
900		135.246		233.940		150.065		75.488		-1205.180		-985.925		57.222
1000		137.957		248.329		159.182		89.147		-1202.658		-961.698		50.234

1100		140.786		261.609		167.897		103.083		-1200.079		-937.726		44.529
1200		143.718		273.984		176.228		117.307		-1197.445		-913.992		39.785
1300		146.741		285.607		184.199		131.830		-1194.750		-890.480		35.780
1400		149.841		296.594		191.839		146.658		-1191.997		-867.177		32.355
1500		153.005		307.040		199.173		161.800		-1189.178		-844.074		29.393

1600		156.221		317.017		206.229		177.261		-1186.283		-821.161		26.808
1700		159.481		326.585		213.029		193.045		-1183.324		-798.431		24.533
1800		162.782		335.794		219.595		209.158		-1180.305		-775.877		22.515
1900		166.112		344.684		225.946		225.603		-1177.243		-753.492		20.715
2000		169.468		353.290		232.099		242.382		-1174.151		-731.269		19.099

2100		172.847		361.640		238.070		259.497		-1171.047		-709.202		17.640
2200		176.246		369.759		243.872		276.952		-1213.709		-687.072		16.313
2300		179.655		377.669		249.518		294.747		-1210.901		-663.196		15.062

2340.000		181.021		380.778		251.736		301.960		II <--> LIQUID

2400		183.086		385.388		255.019		312.884		1207.784 639.449 13.917
2500		186.526		392.931		260.386		331.364		-1204.357		-615.837		12.867

2600		189.978		400.314		265.626		350.189		-1200.617		-592.369		11.901
2700		193.437		407.549		270.749		369.360		-1196.563		-569.051		11.009
2800		196.907		414.646		275.762		388.877		-1192.193		-545.888		10.184
PREVIOUS:								CURRENT: December 1973

Vanadium Oxide (V₂O₃)								O₃V₂(cr)

Download table in tab-delimited text format.