Vanadium Oxide (V2O3)								O3V2(l)
Enthalpy Reference Temperature = Tr = 298.15 K								Standard State Pressure = p° = 0.1 MPa
		J·K-1 mol-1						kJ·mol-1
T/K		Cp°		S°		-[G°-H°(Tr)]/T		H-H°(Tr)		fH°		fG°		log Kf
0
100
200
298.15		104.964		152.250		152.250		0.000		-1093.054		-1029.446		180.355
300		105.260		152.900		152.252		0.194		-1093.033		-1029.051		179.174
400		117.540		185.081		156.556		11.410		-1091.403		-1007.946		131.624
500		123.750		212.069		165.037		23.516		-1089.206		-987.329		103.146
600		127.326		234.974		174.833		36.084		-1086.821		-967.176		84.200
700		130.071		254.813		184.873		48.958		-1084.380		-947.427		70.698
800		132.639		272.350		194.733		62.094		-1081.917		-928.031		60.594
900		135.246		288.123		204.247		75.488		-1079.435		-908.944		52.754
1000		137.957		302.511		213.365		89.147		-1076.912		-890.135		46.496
1100		140.786		315.792		222.080		103.083		-1074.334		-871.582		41.388
1200		143.718		328.167		230.411		117.307		-1071.700		-853.265		37.142
1300		146.741		339.789		238.382		131.830		-1069.004		-835.172		33.558
1400		149.841		350.777		246.021		146.658		-1066.252		-817.287		30.493
1500		152.464		361.210		253.356		161.782		-1063.451		-799.602		27.845
1600		157.846		371.198		260.410		177.261		-1060.537		-782.105		25.533
1600.000		157.846		371.198		260.410		177.261		GLASS <--> LIQUID
1600.000		156.900		371.198		260.410		177.261		TRANSITION
1700		156.900		380.710		267.210		192.951		-1057.674		-764.793		23.499
1800		156.900		389.678		273.767		208.641		-1055.077		-747.641		21.696
1900		156.900		398.162		280.093		224.331		-1052.770		-730.625		20.086
2000		156.900		406.209		286.199		240.021		-1050.767		-713.723		18.641
2100		156.900		413.865		292.098		255.711		-1049.088		-696.914		17.335
2200		156.900		421.164		297.800		271.401		-1093.514		-679.966		16.144
2300		156.900		428.138		303.316		287.091		-1092.811		-661.185		15.016
2340.000		156.900		430.843		305.473		293.367		II <--> LIQUID
2400		156.900		434.816		308.657		302.781		1092.141 642.434 13.982
2500		156.900		441.221		313.832		318.471		-1091.505		-623.709		13.032
2600		156.900		447.374		318.851		334.161		-1090.900		-605.009		12.155
2700		156.900		453.296		323.722		349.851		-1090.326		-586.332		11.343
2800		156.900		459.002		328.452		365.541		-1089.784		-567.675		10.590
2900		156.900		464.508		333.049		381.231		-1089.271		-549.038		9.889
3000		156.900		469.827		337.520		396.921		-1088.787		-530.417		9.235
3100		156.900		474.972		341.871		412.611		-1088.332		-511.812		8.624
3200		156.900		479.953		346.109		428.301		-1087.903		-493.223		8.051
3300		156.900		484.781		350.238		443.991		-1087.500		-474.646		7.513
3400		156.900		489.465		354.265		459.681		-1087.123		-456.079		7.007
3500		156.900		494.013		358.193		475.371		-1086.769		-437.525		6.530
3600		156.900		498.433		362.027		491.061		-1086.439		-418.979		6.079
3700		156.900		502.732		365.772		506.751		-1979.745		-398.042		5.619
3800		156.900		506.916		369.432		522.441		-1976.085		-355.342		4.885
3900		156.900		510.992		373.010		538.131		-1972.548		-312.736		4.189
4000		156.900		514.964		376.509		553.821		-1969.135		-270.222		3.529
PREVIOUS:								CURRENT: December 1973
Vanadium Oxide (V2O3)								O3V2(l)

Download table in tab-delimited text format.