Vanadium Oxide (V2O3)								O3V2(cr,l)
Enthalpy Reference Temperature = Tr = 298.15 K								Standard State Pressure = p° = 0.1 MPa
		J·K-1 mol-1						kJ·mol-1
T/K		Cp°		S°		-[G°-H°(Tr)]/T		H-H°(Tr)		fH°		fG°		log Kf
0		0.000		0.000		INFINITE		-17.476		-1213.971		-1213.971		INFINITE
100		28.627		14.163		179.288		-16.512		-1218.342		-1192.325		622.807
168.800		63.053		38.652		116.725		-13.179		I <--> II
168.800		63.136		48.269		116.725		-11.555		TRANSITION
200		80.107		60.767		107.019		-9.250		-1219.118		-1165.403		304.372
298.15		104.963		98.067		98.067		0.000		-1218.799		-1139.036		199.554
300		105.260		98.717		98.069		0.194		-1218.779		-1138.542		198.238
400		117.540		130.898		102.373		11.410		-1217.149		-1112.018		145.215
500		123.750		157.887		110.854		23.516		-1214.951		-1085.983		113.452
600		127.326		180.791		120.651		36.084		-1212.566		-1060.412		92.317
700		130.071		200.631		130.691		48.958		-1210.125		-1035.245		77.251
800		132.639		218.168		140.550		62.094		-1207.662		-1010.430		65.974
900		135.246		233.940		150.065		75.488		-1205.180		-985.925		57.222
1000		137.957		248.329		159.182		89.147		-1202.658		-961.698		50.234
1100		140.786		261.609		167.897		103.083		-1200.079		-937.726		44.529
1200		143.718		273.984		176.228		117.307		-1197.445		-913.992		39.785
1300		146.741		285.607		184.199		131.830		-1194.750		-890.480		35.780
1400		149.841		296.594		191.839		146.658		-1191.997		-867.177		32.355
1500		153.005		307.040		199.173		161.800		-1189.178		-844.074		29.393
1600		156.221		317.017		206.229		177.261		-1186.283		-821.161		26.808
1700		159.481		326.585		213.029		193.045		-1183.324		-798.431		24.533
1800		162.782		335.794		219.595		209.158		-1180.305		-775.877		22.515
1900		166.112		344.684		225.946		225.603		-1177.243		-753.492		20.715
2000		169.468		353.290		232.099		242.382		-1174.151		-731.269		19.099
2100		172.847		361.640		238.070		259.497		-1171.047		-709.202		17.640
2200		176.246		369.759		243.872		276.952		-1213.709		-687.072		16.313
2300		179.655		377.669		249.518		294.747		-1210.901		-663.196		15.062
2340.000		181.021		380.778		251.736		301.960		II <--> LIQUID
2340.000		156.900		430.843		251.736		419.112		TRANSITION
2400		156.900		434.816		256.263		428.526		-1092.141		-642.434		13.982
2500		156.900		441.221		263.534		444.216		-1091.505		-623.709		13.032
2600		156.900		447.374		270.487		459.906		-1090.900		-605.009		12.155
2700		156.900		453.296		277.149		475.596		-1090.326		-586.332		11.343
2800		156.900		459.002		283.543		491.286		-1089.784		-567.675		10.590
2900		156.900		464.508		289.688		506.976		-1089.271		-549.038		9.889
3000		156.900		469.827		295.605		522.666		-1088.787		-530.418		9.235
3100		156.900		474.972		301.308		538.356		-1088.332		-511.812		8.624
3200		156.900		479.953		306.814		554.046		-1087.903		-493.223		8.051
3300		156.900		484.781		312.134		569.736		-1087.500		-474.646		7.513
3400		156.900		489.465		317.281		585.426		-1087.123		-456.079		7.007
3500		156.900		494.013		322.266		601.116		-1086.769		-437.525		6.530
3600		156.900		498.433		327.098		616.806		-1086.439		-418.979		6.079
3700		156.900		502.732		331.787		632.496		-1979.745		-398.042		5.619
3800		156.900		506.916		336.341		648.186		-1976.085		-355.342		4.885
3900		156.900		510.992		340.767		663.876		-1972.548		-312.736		4.189
4000		156.900		514.964		345.073		679.566		-1969.135		-270.222		3.529
PREVIOUS:								CURRENT: December 1973
Vanadium Oxide (V2O3)								O3V2(cr,l)

Download table in tab-delimited text format.