Tungsten Oxide (WO3)								O3W1(cr,l)
Enthalpy Reference Temperature = Tr = 298.15 K								Standard State Pressure = p° = 0.1 MPa
		J·K-1 mol-1						kJ·mol-1
T/K		Cp°		S°		-[G°-H°(Tr)]/T		H-H°(Tr)		fH°		fG°		log Kf
0		0.000		0.000		INFINITE		-12.349		-837.259		-837.259		INFINITE
100		30.449		18.862		130.106		-11.124		-841.044		-815.973		426.221
200		58.196		49.480		82.212		-6.546		-842.841		-790.036		206.336
298.15		73.139		75.912		75.912		0.000		-842.909		-764.057		133.860
300		73.304		76.365		75.914		0.135		-842.900		-763.568		132.949
400		82.209		98.738		78.904		7.934		-842.022		-737.237		96.273
500		88.641		117.815		84.825		16.495		-840.563		-711.200		74.299
600		93.113		134.397		91.736		25.597		-838.758		-685.493		59.677
700		96.141		148.993		98.894		35.069		-836.769		-660.104		49.258
800		98.239		161.975		105.983		44.794		-834.694		-635.007		41.462
900		99.923		173.645		112.864		54.703		-832.582		-610.173		35.414
1000		101.671		184.261		119.480		64.781		-830.431		-585.575		30.587
1050.000		102.508		189.242		122.684		69.886		I <--> II
1050.000		98.144		190.655		122.684		71.369		TRANSITION
1100		98.963		195.239		125.879		76.296		-826.958		-561.262		26.652
1200		100.601		203.920		132.025		86.275		-825.128		-537.188		23.383
1300		102.238		212.037		137.871		96.417		-823.230		-513.269		20.623
1400		103.875		219.674		143.444		106.722		-821.261		-489.499		18.263
1500		105.512		226.896		148.769		117.192		-819.216		-465.873		16.223
1600		107.149		233.758		153.868		127.825		-817.094		-442.386		14.442
1700		108.787		240.303		158.761		138.621		-814.892		-419.034		12.875
1745.000		109.537		243.155		160.901		143.534		II <--> LIQUID
1745.000		131.796		285.235		160.901		216.963		TRANSITION
1800		131.796		289.325		164.763		224.212		-737.980		-398.147		11.554
1900		131.796		296.451		171.508		237.391		-733.562		-379.388		10.430
2000		131.796		303.211		177.926		250.571		-729.227		-360.860		9.425
2100		131.796		309.641		184.046		263.750		-724.975		-342.546		8.520
2200		131.796		315.772		189.895		276.930		-720.807		-324.433		7.703
2300		131.796		321.631		195.496		290.110		-716.722		-306.508		6.961
2400		131.796		327.240		200.870		303.289		-712.720		-288.759		6.285
2500		131.796		332.620		206.033		316.469		-708.802		-271.175		5.666
2600		131.796		337.790		211.002		329.648		-704.962		-253.746		5.098
2700		131.796		342.764		215.790		342.828		-701.227		-236.462		4.575
2800		131.796		347.557		220.411		356.008		-697.633		-219.314		4.091
2900		131.796		352.182		224.876		369.187		-694.216		-202.294		3.644
3000		131.796		356.650		229.194		382.367		-691.004		-185.386		3.228
PREVIOUS:								CURRENT: September 1966
Tungsten Oxide (WO3)								O3W1(cr,l)

Download table in tab-delimited text format.