		J·K^-1 mol^-1						kJ·mol^-1
Lead Silicate (Pb₂SiO₄)								O₄Pb₂Si₁(cr)

Enthalpy Reference Temperature = T_r = 298.15 K								Standard State Pressure = p° = 0.1 MPa
T/K		C_p^°		S^°		-[G^°-H^°(T_r)]/T		H-H^°(T_r)		_fH^°		_fG^°		log K_f
0		0.000		0.000		INFINITE		-25.932		-1369.466		-1369.466		INFINITE
100		73.789		72.007		291.667		-21.966		-1375.108		-1339.898		699.891
200		113.968		136.700		198.686		-12.397		-1377.589		-1303.493		340.437

298.15		136.984		186.832		186.832		0.000		-1377.875		-1267.007		221.974

300		137.235		187.680		186.835		0.254		-1377.866		-1266.320		220.486
400		152.005		229.255		192.403		14.741		-1376.901		-1229.256		160.524
500		163.762		264.478		203.383		30.547		-1375.118		-1192.537		124.583

600		173.343		295.224		216.181		47.426		-1372.712		-1156.238		100.659
700		180.121		322.489		229.458		65.122		-1379.617		-1118.781		83.484
800		184.180		346.822		242.636		83.349		-1376.607		-1081.721		70.629
900		186.774		368.668		255.447		101.899		-1373.401		-1045.052		60.653
1000		189.117		388.473		267.775		120.699		-1370.045		-1008.747		52.692

1100		190.790		406.580		279.582		139.698		-1366.569		-972.784		46.194
1200		192.046		423.232		290.868		158.836		-1363.015		-937.142		40.793
1300		193.719		438.670		301.651		178.125		-1359.374		-901.800		36.235
1400		195.309		453.086		311.959		197.578		-1355.656		-866.741		32.338
1500		196.648		466.607		321.823		217.177		-1351.892		-831.950		28.971

1600		197.903		479.339		331.273		236.906		-1348.109		-797.410		26.033
1700		199.033		491.371		340.340		256.753		-1394.502		-762.660		23.434
1800		200.121		502.778		349.050		276.710		-1390.499		-725.609		21.057
1900		201.292		513.629		357.429		296.780		-1386.467		-688.780		18.936
2000		202.506		523.985		365.500		316.970		-1382.402		-652.165		17.033

PREVIOUS:								CURRENT: June 1965

Lead Silicate (Pb₂SiO₄)								O₄Pb₂Si₁(cr)

Download table in tab-delimited text format.