Vanadium Oxide (V2O4)								O4V2(l)
Enthalpy Reference Temperature = Tr = 298.15 K								Standard State Pressure = p° = 0.1 MPa
		J·K-1 mol-1						kJ·mol-1
T/K		Cp°		S°		-[G°-H°(Tr)]/T		H-H°(Tr)		fH°		fG°		log Kf
0
100
200
298.15		120.081		173.473		173.473		0.000		-1332.151		-1244.289		217.994
300		120.499		174.217		173.475		0.223		-1332.130		-1243.744		216.555
400		135.281		211.142		178.409		13.093		-1330.330		-1214.523		158.600
500		143.269		242.239		188.151		27.044		-1327.818		-1185.852		123.885
600		148.448		268.835		199.436		41.639		-1324.985		-1157.722		100.789
700		152.175		292.004		211.041		56.674		-1322.010		-1130.079		84.327
800		155.457		312.543		222.469		72.060		-1318.967		-1102.867		72.010
900		158.157		331.011		233.520		87.742		-1315.899		-1076.039		62.452
1000		160.682		347.807		244.122		103.685		-1312.823		-1049.552		54.823
1100		163.033		363.233		254.258		119.872		-1309.748		-1023.374		48.596
1200		165.209		377.513		263.942		136.286		-1306.700		-997.475		43.419
1200.000		165.209		377.513		263.942		136.286		GLASS <--> LIQUID
1200.000		213.384		377.513		263.942		136.286		TRANSITION
1300		213.384		394.593		273.344		157.624		-1298.979		-972.021		39.056
1400		213.384		410.407		282.576		178.963		-1291.523		-947.152		35.339
1500		213.384		425.129		291.595		200.301		-1284.329		-922.807		32.135
1600		213.384		438.900		300.375		221.639		-1277.389		-898.933		29.347
1700		213.384		451.836		308.908		242.978		-1270.723		-875.485		26.900
1800		213.384		464.033		317.191		264.316		-1264.336		-852.422		24.737
1818.000		213.384		466.156		318.655		268.157		II <--> LIQUID
1900		213.384		475.570		325.226		285.655		1258.250 829.705 22.810
2000		213.384		486.515		333.019		306.993		-1252.480		-807.301		21.085
2100		213.384		496.926		340.578		328.331		-1247.045		-785.177		19.530
2200		213.384		506.853		347.912		349.670		-1287.728		-763.093		18.118
2300		213.384		516.338		355.030		371.008		-1283.291		-739.346		16.791
2400		213.384		525.420		361.942		392.347		-1278.900		-715.792		15.579
2500		213.384		534.131		368.657		413.685		-1274.552		-692.418		14.467
2600		213.384		542.500		375.183		435.023		-1270.247		-669.218		13.445
2700		213.384		550.553		381.530		456.362		-1265.984		-646.182		12.501
2800		213.384		558.313		387.706		477.700		-1261.761		-623.303		11.628
2900		213.384		565.801		393.719		499.039		-1257.579		-600.576		10.818
3000		213.384		573.035		399.576		520.377		-1253.435		-577.991		10.064
PREVIOUS:								CURRENT: June 1973
Vanadium Oxide (V2O4)								O4V2(l)

Download table in tab-delimited text format.