		J·K^-1 mol^-1						kJ·mol^-1
Vanadium Oxide (V₂O₄)								O₄V₂(cr,l)

Enthalpy Reference Temperature = T_r = 298.15 K								Standard State Pressure = p° = 0.1 MPa
T/K		C_p^°		S^°		-[G^°-H^°(T_r)]/T		H-H^°(T_r)		_fH^°		_fG^°		log K_f
0		0.000		0.000		INFINITE		-18.100		-1418.617		-1418.617		INFINITE
100		36.907		18.652		186.891		-16.824		-1424.127		-1389.894		726.006
200		90.274		62.333		113.357		-10.205		-1427.002		-1354.252		353.694

298.15		115.399		103.525		103.525		0.000		-1427.162		-1318.445		230.986

300		115.787		104.240		103.527		0.214		-1427.150		-1317.770		229.444

340.000		123.336		119.218		104.501		5.004		I <--> II
340.000		127.621		145.675		104.501		13.999		TRANSITION

400		135.281		167.065		112.309		21.902		-1416.532		-1283.094		167.555
500		143.269		198.162		126.456		35.853		-1414.020		-1250.016		130.588

600		148.448		224.758		140.677		50.448		-1411.187		-1217.477		105.991
700		152.175		247.927		154.379		65.483		-1408.212		-1185.426		88.458
800		155.457		268.466		167.380		80.868		-1405.169		-1153.807		75.336
900		158.157		286.934		179.655		96.551		-1402.101		-1122.571		65.152
1000		160.682		303.729		191.236		112.494		-1399.025		-1091.677		57.023

1100		162.987		319.153		202.173		128.678		-1395.953		-1061.091		50.387
1200		165.209		333.430		212.523		145.089		-1392.908		-1030.784		44.869
1300		167.330		346.738		222.341		161.716		-1389.898		-1000.729		40.210
1400		169.406		359.215		231.677		178.553		-1386.944		-970.904		36.225
1500		171.429		370.972		240.575		195.595		-1384.045		-941.289		32.779

1600		173.427		382.100		249.076		212.838		-1381.201		-911.865		29.769
1700		175.302		392.669		257.214		230.273		-1378.439		-882.616		27.119
1800		177.343		402.746		265.022		247.904		-1375.760		-853.528		24.769

1818.000		177.728		404.513		266.394		251.100		II <--> LIQUID
1818.000		213.384		466.156		266.394		363.168		TRANSITION

1900		213.384		475.570		275.220		380.666		-1258.250		-829.705		22.810
2000		213.384		486.515		285.513		402.004		-1252.480		-807.301		21.085

2100		213.384		496.926		295.335		423.342		-1247.045		-785.177		19.530
2200		213.384		506.853		304.725		444.681		-1287.728		-763.093		18.118
2300		213.384		516.338		313.721		466.019		-1283.291		-739.346		16.791
2400		213.384		525.420		322.354		487.358		-1278.900		-715.792		15.579
2500		213.384		534.131		330.652		508.696		-1274.552		-692.418		14.467

2600		213.384		542.500		338.640		530.034		-1270.247		-669.218		13.445
2700		213.384		550.553		346.341		551.373		-1265.984		-646.182		12.501
2800		213.384		558.313		353.773		572.711		-1261.761		-623.303		11.628
2900		213.384		565.801		360.956		594.050		-1257.579		-600.576		10.818
3000		213.384		573.035		367.906		615.388		-1253.435		-577.991		10.064

PREVIOUS:								CURRENT: December 1973

Vanadium Oxide (V₂O₄)								O₄V₂(cr,l)

Download table in tab-delimited text format.