Titanium Oxide (Ti4O7) O7Ti4(l)
 
Enthalpy Reference Temperature = Tr = 298.15 K Standard State Pressure = p° = 0.1 MPa
  J·K-1 mol-1 kJ·mol-1  
T/K Cp° S° -[G°-H°(Tr)]/T H-H°(Tr) fH° fG° log Kf
0              
100              
200              
 
298.15 208.489 291.066 291.066 0.000 -3216.035 -3052.056 534.708
 
300 209.200 292.358 291.070 0.386 -3216.026 -3051.039 531.233
400 239.911 357.091 299.687 22.961 -3214.304 -2996.243 391.269
500 258.864 412.821 316.877 47.972 -3210.960 -2942.090 307.358
 
600 271.165 461.174 336.989 74.511 -3206.781 -2888.699 251.484
700 279.659 503.647 357.826 102.075 -3202.160 -2836.046 211.628
800 285.976 541.423 378.458 130.372 -3197.242 -2784.078 181.782
900 290.830 575.396 398.484 159.221 -3192.277 -2732.732 158.604
1000 294.805 606.249 417.742 188.508 -3187.591 -2681.926 140.089
 
1100 298.152 634.508 436.181 218.159 -3183.482 -2631.564 124.963
1200 301.081 660.578 453.809 248.123 -3195.917 -2581.068 112.351
1300 303.675 684.782 470.656 278.364 -3190.139 -2530.066 101.659
 
1300.000 303.675 684.782 470.656 278.364 GLASS <--> LIQUID
1300.000 368.192 684.782 470.656 278.364 TRANSITION
 
1400 368.192 712.068 486.937 315.183 -3178.202 -2479.742 92.520
1500 368.192 737.471 502.803 352.002 -3166.728 -2430.256 84.629
 
1600 368.192 761.233 518.220 388.821 -3155.763 -2381.518 77.749
1700 368.192 783.555 533.178 425.641 -3145.356 -2333.450 71.698
1800 368.192 804.600 547.678 462.460 -3135.557 -2285.977 66.337
1900 368.192 824.507 561.729 499.279 -3126.417 -2239.030 61.555
 
1950.000 368.192 834.071 568.590 517.689 CRYSTAL <--> LIQUID
 
2000 368.192 843.393 575.344 536.098 3176.735 2190.733 57.216
 
2100 368.192 861.357 588.539 572.917 -3172.060 -2141.548 53.268
2200 368.192 878.485 601.332 609.737 -3167.465 -2092.582 49.684
2300 368.192 894.852 613.741 646.556 -3162.948 -2043.826 46.417
2400 368.192 910.522 625.783 683.375 -3158.509 -1995.265 43.426
2500 368.192 925.553 637.475 720.194 -3154.147 -1946.887 40.678
 
2600 368.192 939.993 648.834 757.013 -3149.859 -1898.681 38.145
2700 368.192 953.889 659.877 793.833 -3145.645 -1850.638 35.803
2800 368.192 967.279 670.618 830.652 -3141.503 -1802.750 33.631
2900 368.192 980.200 681.072 867.471 -3137.430 -1755.012 31.611
3000 368.192 992.682 691.252 904.290 -3133.426 -1707.410 29.729
 
3100 368.192 1004.755 701.171 941.109 -3129.486 -1659.939 27.970
3200 368.192 1016.445 710.842 977.929 -3125.610 -1612.599 26.323
3300 368.192 1027.774 720.275 1014.748 -3121.795 -1565.377 24.778
3400 368.192 1038.766 729.482 1051.567 -3118.037 -1518.268 23.325
3500 368.192 1049.439 738.472 1088.386 -3114.337 -1471.271 21.958
 
3600 368.192 1059.811 747.254 1125.205 -3110.690 -1424.377 20.667
3700 368.192 1069.899 755.839 1162.025 -4743.489 -1346.433 19.008
3800 368.192 1079.718 764.233 1198.844 -4735.007 -1254.732 17.247
3900 368.192 1089.282 772.446 1235.663 -4726.794 -1163.252 15.580
4000 368.192 1098.604 780.484 1272.482 -4718.845 -1071.983 13.999
 